一种自制食物废油咪唑啉衍生物缓蚀剂的性能

发布时间：2018-05-28 22:45

  本文选题：缓蚀剂 + 食物废油原料　； 参考：《腐蚀与防护》2017年01期

【摘要】：以食物废油、对羟基二苯胺和三乙胺为原料得到咪唑啉中间体,用苯丙乳液、偶联剂和消泡剂等对其进行改性,得到稳定的咪唑啉衍生物缓蚀剂。采用红外光谱法对该咪唑啉缓蚀剂进行了分析,采用静态失重法、电化学法和扫描电子显微镜研究了其对J55钢的缓蚀行为,并探讨了其在J55钢表面的吸附行为。结果表明,该缓蚀剂为阳离子型缓蚀剂,当其质量浓度为500mg/L时,在试验溶液中对J55钢的缓蚀率达到87.97%,且吸附满足Langmuir等温吸附方程。
[Abstract]:Imidazoline intermediates were prepared from food waste oil, p-hydroxydiphenylamine and triethylamine, modified by styrene-acrylic emulsion, coupling agent and defoamer, and a stable inhibitor of Imidazoline derivatives was obtained. The corrosion inhibitor of Imidazoline was analyzed by infrared spectroscopy. The corrosion inhibition behavior of Imidazoline on J55 steel was studied by static weight loss method, electrochemical method and scanning electron microscope, and its adsorption behavior on the surface of J55 steel was discussed. The results show that the inhibitor is a cationic corrosion inhibitor. When the mass concentration of the inhibitor is 500mg/L, the corrosion inhibition rate of J55 steel in the test solution reaches 87.97, and the adsorption satisfies the Langmuir isothermal adsorption equation.
【作者单位】： 延长油田股份有限公司杏子川采油厂;西南石油大学石油与天然气工程学院;西南石油大学油气消防四川省重点实验室;中国石油集团工程设计有限责任公司西南分公司;
【分类号】：TG174.42

【相似文献】

相关期刊论文 前10条

1 吕洪久;;日本将用新法制造咪唑啉酮[J];精细与专用化学品;1985年06期

2 徐长卿;用椰子油直接合成咪唑啉及其衍生物[J];日用化学工业;1985年02期

3 马慰霖;沈中原;庄义婷;;2-咪唑啉酮合成的新工艺[J];农药;1986年03期

4 任晋斌;咪唑啉型香波原料安全性试验[J];日用化学工业;1987年05期

5 储宁启,张晓生,李湘林;咪唑啉环化釜改造[J];日用化学工业;1990年05期

6 丁渝;沈苗;周宁;;1-苄基-5-乙氧基-2,4-咪唑啉二酮的合成[J];化学试剂;1993年01期

7 赵炳筠,郭艳玲,王进东,夏炽中;1,2,3—三取代咪唑啉盐的质谱研究[J];山西大学学报(自然科学版);1997年03期

8 谢晖,何文深,周永红;松香基咪唑啉的合成及应用[J];南京工业大学学报(自然科学版);2004年06期

9 焦其正;付朝阳;王丽荣;郑家q，

本文编号：1948475