选区激光熔化工艺参数对Ti-6Al-4V成形质量的影响

发布时间：2018-05-29 08:00

本文选题：选区激光熔化 + 增材制造　；参考：《材料导报》2017年10期

【摘要】：选区激光熔化是一种利用高能束选择性熔化金属粉末进而直接制造复杂几何形状产品的增材制造技术。采用选区激光熔化成形Ti-6Al-4V样品,分析影响选区激光熔化成形质量的主要因素,采用体式显微镜、金相显微镜、扫描电子显微镜(SEM)、显微硬度计系统研究了不同工艺参数对Ti-6Al-4V合金选区激光熔化成形样品的表面形貌、致密度、组织、显微硬度的影响规律。研究得出Ti-6Al-4V合金选区激光熔化成形的优选工艺参数为:扫描功率450W,扫描速度2 500mm/s,扫描间距0.07mm,该工艺参数下打印出的样品具有较为优良的成形质量,致密度高达97.8%,显微硬度平均值为446HV。
[Abstract]:Selective laser melting is a kind of material augmentation technology which uses high energy beam selective melting of metal powder to produce complex geometry products directly. The main factors affecting the quality of selective laser melting forming (Ti-6Al-4V) were analyzed by selective laser melting forming (Ti-6Al-4V) samples. The effect of different process parameters on the surface morphology, density, microstructure and microhardness of selected laser melt forming samples of Ti-6Al-4V alloy was studied by scanning electron microscope (SEM) and microhardness tester. The optimum parameters of laser melting forming of Ti-6Al-4V alloy are as follows: scanning power 450 W, scanning speed 2 500 mm / s, scanning distance 0.07 mm. The density is as high as 97.8 and the average microhardness is 446HV.
【作者单位】：广东省科学院广东省材料与加工研究所;山东大学材料科学与工程学院;西安理工大学材料科学与工程学院;广东汉邦激光科技有限公司;
【基金】：广东省金属强韧化技术与应用重点实验室(2014B030301012) 广州市先进金属结构材料重点实验室(201509010003) 广东省重大科技专项(2014B010131005) 广东省金属材料与加工专业镇联合创新公共平台(2013B091602002) 广东省产学研项目(2014B090907008) 广东省重大项目(2016B090914001)
【分类号】：TG665