经电脉冲处理的轧制AZ31镁合金组织与性能演变

发布时间：2018-06-03 07:06

本文选题：AZ镁合金 + 脉冲电流处理　；参考：《稀有金属材料与工程》2017年09期

【摘要】：利用超景深显微镜、扫描电镜(SEM)、电子背散射衍射(EBSD)研究了高能量脉冲电流对10%、15%、20%不同轧制变形量AZ31镁合金组织演化与力学性能的影响。当变形量为20%的轧制板材经电流密度为4.16×10~9 A/m~2、脉宽为30μs、频率为100 Hz的脉冲电流处理10 min后,平均晶粒尺寸由150μm细化至20μm,抗拉强度提升至265 MPa,伸长率可达19.7%。同时,分析了此实验参数下电脉冲处理过程中热效应与非热效应对再结晶的影响,发现热效应在再结晶过程中占主导作用,并揭示了非热效应的作用机理。
[Abstract]:The effects of high energy pulse current on the microstructure evolution and mechanical properties of AZ31 magnesium alloy with different rolling deformation of 1015% and 20% have been studied by means of hyperfield microscope, scanning electron microscope and electron backscatter diffraction (EBSD). When the current density, pulse width and frequency of 20% of the rolled sheet are 4.16 脳 10 ~ (9) A / m ~ (2), 30 渭 s and 10 min, the average grain size is refined from 150 渭 m to 20 渭 m, the tensile strength is increased to 265 MPA, and the elongation can reach 19.7m. At the same time, the effects of thermal and non-thermal effects on recrystallization under the experimental parameters are analyzed. It is found that the thermal effect plays a dominant role in the recrystallization process, and the mechanism of non-thermal effect is revealed.
【作者单位】：太原理工大学新材料界面科学与工程教育部重点实验室;太原理工大学先进镁基材料山西省重点实验室;太原理工大学山西省新材料工程技术研究中心;太原理工大学材料科学与工程学院;
【基金】：国家自然科学基金(51504162,50901048,51174143) 教育部新世纪优秀人才支持计划(NCET-12-1040);教育部科学技术研究重点项目(2012017) 山西省自然科学基金(2015011033,2015021073) 山西省高等学校科技创新项目(2014118) 山西省留学人员科技活动择优资助项目太原理工大学2014年校专项/青年基金(2014TD016)
【分类号】：TG146.22;TG661