轧制工艺对汽车用镁合金微观组织和力学性能的影响

发布时间：2018-06-05 11:09

  本文选题：镁合金 + 轧制　； 参考：《热加工工艺》2017年01期

【摘要】：研究了轧制工艺对镁合金微观组织和力学性能的影响。结果表明,随着轧制道次的增加,镁合金组织中孪晶组织越来越多。随着轧制温度的提高,镁合金变形能力增加,但晶粒长大,且氧化程度加剧。镁合金抗拉强度、屈服强度和伸长率随轧制道次增加而升高。随轧制温度增加,镁合金抗拉强度和屈服强度降低,伸长率升高。
[Abstract]:The effect of rolling process on microstructure and mechanical properties of magnesium alloy was studied. The results show that with the increase of rolling pass, there are more and more twinning microstructure in magnesium alloy. With the increase of rolling temperature, the deformation ability of magnesium alloy increases, but the grain grows and the oxidation degree increases. The tensile strength, yield strength and elongation of magnesium alloy increased with the increase of rolling pass. With the increase of rolling temperature, the tensile strength and yield strength of magnesium alloy decrease, and the elongation of magnesium alloy increases.
【作者单位】： 河南职业技术学院;
【基金】：河南省教育厅自然科学基金资助项目(200310824001)
【分类号】：TG146.22;TG339

【相似文献】

相关期刊论文 前10条

1 凌军;徐进;陈明刚;李云龙;;轧制道次不变扩大钢坯断面[J];黑龙江冶金;1998年01期

2 许磊;曾庆亮;崔海涛;王国栋;;扩展卡尔曼滤波在中厚板轧制道次修正中的应用[J];东北大学学报(自然科学版);2010年03期

3 苗雨川;;简析厚板轧制道次规程的设定[J];宝钢技术;2006年04期

4 刘少斌;王健;李佩;顾彬;卫思璇;周世平;;轧制道次变形量对AgCuNi/TU1复合材料板形的影响[J];贵金属;2010年02期

5 赵田丽;张兵;袁守谦;陈忠伟;;ARB制备6063Al/MB2/6063Al复合材料的组织和性能[J];热加工工艺;2011年08期

6 关学丰,李春迎,关尔滨,黄立寰;减少LF2Y合金箔轧制道次的工艺研究[J];轻金属;1997年06期

7 张明祥;来晓君;贾东明;;宽钼板轧制过程中宽展量的研究[J];西安工业大学学报;2006年01期

8 郭伟;董占斌;张跃飞;沈开照;郑会平;黄少帅;;400mm厚连铸坯轧制高韧性特厚板技术开发[J];轧钢;2013年01期

9 刘志宏;郁杰;吴杰峰;李波;;CICC导体轧制过程有限元模拟[J];核聚变与等离子体物理;2008年01期

10 吴光亮,成小军,焦国华,罗钢,孟征兵;BOF-LF-CSP工艺生产低碳热轧薄板的组织变化规律[J];湖南冶金;2005年06期

相关会议论文 前1条

1 苗雨川;刘健;;厚板轧制道次规程设定简介[A];2006年全国轧钢生产技术会议文集[C];2006年

相关重要报纸文章 前2条

1 廖建国;超细晶薄钢板超短时间间隔多道次轧制技术的开发[N];世界金属导报;2005年

2 包斯文;三大因素导致上海小规格螺纹钢紧缺[N];中国冶金报;2013年

相关硕士学位论文 前1条

1 韩跃;钢板表面划痕轧制过程中演变规律的研究[D];辽宁科技大学;2012年

，

本文编号：1981776