冷却工艺对Q345钢轧制过程中金属变形的影响

发布时间：2018-06-12 12:49

  本文选题：中厚板 + 温控形变耦合轧制　； 参考：《上海金属》2017年06期

【摘要】：受原始坯规格或轧机能力限制,厚板轧制压下率不足将使轧制变形难以向轧件心部渗透,导致连铸坯原始内部缺陷难以消除、钢板组织粗化等问题,影响最终产品的质量。研究了通过控制轧制过程中的冷却工艺,实现温控和变形耦合的轧制工艺,旨在通过厚向大温度梯度轧制增强轧件的变形渗透性。重点研究了轧件厚向相同心表温差不同温度梯度条件对金属塑性变形的影响。
[Abstract]:Due to the limitation of the original billet specification or mill capacity, the insufficient rolling reduction rate of thick plate will make the rolling deformation difficult to penetrate into the center of the rolling piece, resulting in the original internal defects of the continuous casting billet being difficult to eliminate and the steel plate structure coarsening, which will affect the quality of the final product. The coupling of temperature control and deformation is realized by controlling the cooling process in the rolling process. The purpose of this paper is to enhance the deformation permeability of the workpiece by thick and large temperature gradient rolling. The influence of different temperature gradient conditions on metal plastic deformation is studied.
【作者单位】： 东北大学轧制技术及连轧自动化国家重点实验室;
【分类号】：TG335

【相似文献】

相关期刊论文 前5条

1 李林生;李国莱;陈云生;;温度梯度下介质在高分子平板材料中的扩散[J];中国腐蚀与防护学报;1988年04期

2 陈伟昌，Ｈ．Ｓ．Ｆｅｒｇｕｓｏｎ，韦东滨，贺毓辛;金属加工温度梯度及其不等温韧性[J];钢铁;1997年09期

3 付君伟;温度梯度是热矫正的关键[J];一重技术;2000年01期

4 侯乃先;岳珠峰;于庆民;虞跨海;朱振涛;;温度梯度下薄壁圆管试件拉伸性能的试验与理论研究[J];材料工程;2008年03期

5 蔡英文，李建国，毛协民，傅恒志;超高温度梯度场中的Al－Bi偏晶共生行为[J];材料研究学报;1995年03期

相关会议论文 前2条

1 陶宇;张国星;刘建涛;;粉末涡轮盘温度梯度热处理工装设计研究[A];第十二届中国高温合金年会论文集[C];2011年

2 杨书营;何荣曦;孙进;;改变温度梯度开发QT600飞轮[A];重庆市机械工程学会铸造分会、重庆铸造行业协会2010重庆市铸造年会论文集[C];2010年

相关博士学位论文 前1条

1 张志超;5A06铝合金中厚板差温反拉深成形规律研究[D];哈尔滨工业大学;2016年

相关硕士学位论文 前2条

1 刘硕;焊点联接中间相中与温度和电流场相关问题的计算[D];哈尔滨工业大学;2016年

2 杜隆纯;基于温度梯度诱发的微焊点显微组织演变研究[D];华南理工大学;2015年

，

本文编号：2009727