核电用SA-508 Gr.3 Cl.2钢带极电渣堆焊工艺

发布时间：2018-06-12 22:34

  本文选题：核电 + 电渣堆焊　； 参考：《化工设备与管道》2016年06期

【摘要】：根据某核电项目要求,对堆焊要求的分析和堆焊方法的选择,通过带极电渣堆焊评定对堆焊金属进行拉伸、弯曲、化学成分、铁素体数、晶间腐蚀、硬度、金相的分析试验,结果满足标准和项目要求。试验结果表明,采用合理的措施和合适的焊接参数,使用电渣带极堆焊能获得优异焊接接头,并成功对产品的SA-508 Gr.3 Cl.2进行大面积不锈钢带极电渣堆焊。
[Abstract]:According to the requirements of a nuclear power project, the analysis of surfacing requirements and the selection of surfacing methods are carried out, and the tensile, bending, chemical composition, ferrite number, intergranular corrosion, hardness, metallographic analysis of the surfacing metal are tested through the assessment of the surfacing metal with electrode electroslag surfacing. The results meet the standards and project requirements. The test results show that the excellent welding joint can be obtained by using reasonable measures and proper welding parameters, and a large area of stainless steel strip electrode electroslag surfacing welding is successfully carried out on SA-508 Gr.3 Cl.2.
【作者单位】： 上海森松压力容器有限公司;中国中原对外工程有限公司;
【分类号】：TG455

【相似文献】

相关期刊论文 前10条

1 ;磁控带极电渣堆焊技术研究成果[J];压力容器;1987年03期

2 ;为扩大电渣焊应用范W Ru造新法 躺板iu电渣堆焊奻歐[J];焊接;1959年03期

3 王文功;;躺板极电渣堆焊[J];机械工人;1960年05期

4 孙松年;造船用低稀释电渣堆焊[J];造船技术;1991年06期

5 孙剑虹,叶栋林;不锈钢一带一剂双层电渣堆焊工艺[J];焊接;1997年03期

6 吕燕;带极电渣堆焊在核电产品中的应用[J];压力容器;1997年02期

7 ;，

本文编号：2011321