基于曲率积分的双金属复合板辊式矫直过程解析

发布时间：2018-06-15 12:25

  本文选题：矫直 + 双金属复合板　； 参考：《浙江大学学报(工学版)》2017年08期

【摘要】：分析双金属复合板矫直过程的截面弯曲特性,建立双金属复合板任意加卸载时的弯矩-曲率关系.对矫直过程的板材进行划分,弹性矫直区间段根据弹性加载的弯矩-曲率关系积分求解曲率变化量积分值,弹塑性矫直区间段按曲率差值等分离散后求解曲率变化量积分值,建立双金属复合板曲率积分解析模型.解析了钢-铝复合板辊式矫直过程,与单一材料板材的矫直过程进行对比.结果表明,钢-铝复合板在矫直过程中会出现中性层偏移.矫后钢-铝复合板基层残余应力较小而覆层发生反向屈服.反向屈服会削弱复合板的回弹,且具有累积效应.
[Abstract]:The bending behavior of bimetallic composite plate during straightening process is analyzed and the relationship between bending moment and curvature of bimetallic composite plate under arbitrary loading and unloading is established. The plates in the process of straightening are divided. The integral value of curvature variation is solved according to the integral of bending moment curvature relation under elastic loading, and the integral value of curvature change is solved by separating the section of elastic-plastic straightening interval according to curvature difference. An analytical model of curvature integral for bimetallic composite plates is established. The roller straightening process of steel-aluminum composite plate was analyzed and compared with that of single material plate. The results show that the neutral layer migration occurs in the straightening process of steel-aluminum composite plate. After correction, the residual stress of steel-aluminum composite plate base is small and the cladding produces reverse yield. Reverse yield weakens the springback of the composite plate and has a cumulative effect.
【作者单位】： 北京科技大学机械工程学院;
【分类号】：TG301

【相似文献】

相关会议论文 前2条

1 刘红娜;;辊式矫直对冷轧板板形的影响[A];第二届薄钢板质量研讨会论文集[C];2002年

2 马重立;张晓丽;肖春安;谈海娟;杨雷;;5754-H111铝合金φ30 mm×2.5 mm高精级薄壁管的生产工艺研究[A];全国第十四届轻合金加工学术交流会论文集[C];2009年

相关硕士学位论文 前4条

1 李艳威;辊式矫直过程残余应力测试与分析[D];太原科技大学;2015年

2 杨晓君;中厚板辊式矫直过程算法模型修正[D];太原科技大学;2011年

3 高聪敏;带材辊式矫直过程的有限元分析[D];太原科技大学;2008年

4 王海澜;双金属复合板材辊式矫直计算模型建立及研究[D];太原科技大学;2014年

，

本文编号：2022004