Cr12MoV模具钢中性盐浴渗钛组织与性能

发布时间：2018-06-19 06:35

  本文选题：CrMoV钢 + 铬钛共渗　； 参考：《特种铸造及有色合金》2017年01期

【摘要】：采用TD技术在小型井式盐浴炉中对Cr12MoV钢分别进行了渗钛、铬钛共渗、铬钛复合渗中性盐浴处理。测试分析了覆层的显微组织、物相结构、厚度、硬度、耐磨性和耐腐蚀性。结果表明,Cr12MoV中性盐浴渗钛、铬钛共渗和铬钛复合渗覆层的显微硬度(HV0.05)都超过了3 000;铬钛共渗和铬钛复合渗覆层的显微硬度呈现梯度变化;渗钛、铬钛共渗和铬钛复合渗覆层的耐磨性和耐腐蚀性较基体有很大提高。
[Abstract]:Cr12MoV steel was treated by TD technique in a small well type salt bath furnace. The steel was treated with titanium infiltration, chromium-titanium co-infiltration and chromium-titanium composite infiltration in neutral salt bath respectively. The microstructure, phase structure, thickness, hardness, wear resistance and corrosion resistance of the coating were analyzed. The results show that the microhardness of Cr _ (12) Mo _ (V), Cr _ (12) Mo _ (V) and Cr _ (2 +) Ti _ (2 +) / Cr _ (2 +) / Ti _ (2 +) / Cr _ (12) Ti _ (10) / Cr _ (12) TIO _ (2) / Cr _ (12) Ti _ (2 +) / Cr _ (12) Ti _ ( The wear resistance and corrosion resistance of Cr-Ti and Cr-Ti composite coating are much higher than that of matrix.
【作者单位】： 武汉科技大学钢铁冶金及资源利用省部共建教育部重点实验室;中北大学机械与动力工程学院;
【基金】：国家自然科学基金资助项目(51375353) 高等学校博士学科点专项科研基金资助项目(20131420120002)
【分类号】：TG174.4

【相似文献】

相关期刊论文 前10条

1 谢燮揆;;钢的渗钛[J];新技术新工艺;1984年01期

2 张定儿;毕士庆;朱鸣芳;李根金;徐安达;;粒状渗钛剂的研究[J];金属热处理;1991年01期

3 黄济元;肖继闯;欧阳军;邹敢锋;袁叔贵;;粉末渗钛的研究[J];金属热处理;1991年02期

4 楼白扬,戚九皋;真空固体渗钛及其动力学的研究[J];浙江工学院学报;1992年02期

5 王俊民,高国庆;钢的低真空粉末渗钛[J];金属热处理;1997年01期

6 陈为为;何业东;王德仁;;机械能作用下中温快速制备渗钛涂层的研究[J];装备环境工程;2007年03期

7 М.В.Ситкевич;Е.И.Беиъскни;В.А.Рогов;刘先曙;;渗钛剂成分[J];国外化学热处理;1983年02期

8 刘先曙;;渗钛工艺的发展及其应用[J];国外金属热处理;1986年03期

9 徐重;范本惠;潘俊德;郑维能;;双层辉光离子渗钛[J];金属热处理;1986年05期

10 王贞申 ,程德刚 ,李深涛;熔融盐电解渗钛工艺的初步研究[J];湖北汽车工业学院学报;1989年00期

相关会议论文 前2条

1 陈为为;何业东;王德仁;;中温快速制备渗钛涂层[A];第六届全国表面工程学术会议论文集[C];2006年

2 陈为为;何业东;王德仁;;中温快速制备渗钛涂层[A];第六届全国表面工程学术会议暨首届青年表面工程学术论坛论文集[C];2006年

相关硕士学位论文 前1条

1 刘伟燕;316L不锈钢表面等离子钛合金化及相关性能研究[D];太原理工大学;2010年

，

本文编号：2038932