显微组织均匀性对片层Ti-55531合金高周疲劳裂纹萌生的影响

发布时间：2018-07-01 08:09

  本文选题：Ti-钛合金 + 组织均匀性　； 参考：《稀有金属材料与工程》2017年03期

【摘要】：采用高周拉压疲劳试验,测试了片层Ti-55531合金的室温高周疲劳性能。利用TEM、SEM等分析检测方法,研究了近裂纹源区次生裂纹特征,以及显微组织均匀性对高周疲劳裂纹萌生的影响。结果发现:该片状Ti-55531合金室温高周疲劳强度σ_(-1)(1×10~7)可达639 MPa。合金显微组织中含少量晶界α和大量10~50μm大小的组织不均匀区,疲劳变形时,晶界α处开裂或组织不均匀区内次生αs断裂、α_s/β_r界面处开裂等萌生微裂纹,促进合金的疲劳失效。
[Abstract]:The high cycle fatigue properties of lamellar Ti-55531 alloy at room temperature were tested by high cycle tensile compression fatigue test. The characteristics of secondary crack near crack source and the effect of microstructure uniformity on the initiation of high cycle fatigue crack were studied by means of TEM SEM and other analytical methods. The results show that the high cycle fatigue strength 蟽 _ (-1) (1 脳 10 ~ (7) of the sheet Ti-55531 alloy at room temperature can reach 639 MPA. The microstructure of the alloy contains a small amount of grain boundary 伪 and a large amount of 1050 渭 m inhomogeneous microstructure. During fatigue deformation, the crack at the grain boundary 伪 or the secondary 伪 s fracture in the inhomogeneous region of the grain boundary, the crack at the interface of 伪 s / 尾 -r, and so on, promote the fatigue failure of the alloy.
【作者单位】： 西北工业大学凝固技术国家重点实验室;西北有色金属研究院;
【基金】：国家自然科学基金项目(51471136) 国家国际科技合作(中法合作)项目(2015DFA1430)
【分类号】：TG146.23

【相似文献】

相关期刊论文 前10条

1 马雷;;缓冲器的强度校核应考虑高周疲劳[J];化工设计通讯;1990年02期

2 朱晓阳;奚建法;;低碳钢在高周疲劳循环下的循环硬化问题研究[J];机械强度;1991年02期

3 蔡俊鸿;;探讨延长高周疲劳零件寿命的某些途径[J];四川冶金;1993年03期

4 关昕;孟延军;;超高周疲劳的研究进展[J];钢铁研究;2009年01期

5 张海威;何宇廷;程礼;高潮;张腾;;钛合金超高周疲劳性能试验研究[J];航空材料学报;2013年03期

6 邓瑛;韩秀全;邵杰;邓武警;;钛合金三层空心结构模拟件设计及高周疲劳实验[J];航空制造技术;2013年16期

7 王红卫，杨大智，陈，

本文编号：2087127