一种增材与减材复合制造机研究

发布时间：2018-07-06 13:59

  本文选题：复合加工 + 熔融增材制造　； 参考：《制造技术与机床》2017年06期

【摘要】：为了综合增材制造与减材加工的优点,研制了一台熔融增材制造与铣削减材复合加工机,采用龙门结构,总体尺寸为700 mm×640 mm×780 mm。该机床有3个直线轴和一个回转轴,控制系统采用MACH3控制系统。机床结构采用有限元软件Abaqus进行了优化和分析,并制造了样机。针对PEEK材料脊柱融合器,在该样机上进行了增材与减材制造,验证了所研发机床的性能以及该复合制造机床在医疗PEEK材料增减材制造的潜力。
[Abstract]:In order to synthesize the advantages of material increasing manufacture and material reducing processing, a compound processing machine for melting material increasing and milling and reducing material was developed. The gantry structure was adopted. The overall size of the machine was 700 mm 脳 640 mm 脳 780 mm. The machine tool has three straight axes and one rotary axis, and the control system adopts MACH3 control system. The structure of the machine is optimized and analyzed by finite element software Abaqus, and a prototype is made. In view of peek material spinal fusion cage, the material increasing and reducing materials were manufactured on the prototype. The properties of the developed machine tool and the potential of the composite manufacturing machine tool in the medical peek material were verified.
【作者单位】： 山东理工大学机械工程学院;
【基金】：山东省自然科学基金(ZR2015EL023) 山东省重点研发计划项目(2016GGX103015)
【分类号】：TG65

【相似文献】

相关期刊论文 前6条

1 林宗腾;;单层硅酸乙酯复合制壳工艺及应用[J];机械开发;1992年02期

2 黄淑梅;轧制复合制造Ti-Al系金属间化合物板材[J];稀有金属材料与工程;2001年04期

3 潘启英;吴锦荣;黄光速;何显儒;;丁基橡胶/丙烯酸酯橡胶共混物-钢片复合制件的粘接性能[J];合成橡胶工业;2007年01期

4 ;专利信息[J];稀有金属快报;2008年06期

5 雒娅楠,邱志刚,宋诗哲,董飒英,王洪仁,于辉;PVD法及与电镀复合制备光纤腐蚀传感器的Fe-C合金敏感膜[J];化工学报;2004年06期

6 ;[J];;年期

相关会议论文 前1条

1 雒娅楠;邱志刚;宋诗哲;董飒英;王洪仁;于辉;;PVD与电镀复合制备光纤腐蚀传感器的Fe-C合金敏感膜[A];2004年腐蚀电化学及测试方法学术交流会论文集[C];2004年

相关硕士学位论文 前1条

1 周火金;复杂叶轮零件的熔积—铣削复合制造研究[D];华中科技大学;2012年

，

本文编号：2103007