改性SiC_p在无缸套灰铸铁气缸体材质开发中的应用

发布时间：2018-07-08 16:20

  本文选题：改性SiC_p + 无缸套气缸体　； 参考：《铸造》2017年11期

【摘要】：无缸套缸体材质无法达到耐磨性的设计要求,不得不在缸孔镶薄壁缸套。通过加入微量改性SiC_p强化HT250的刚性、耐磨性,经过摩擦磨损试验,缸孔变形量测试及台架试验等方法验证其效果。结果表明,加入微量改性SiC_p后的HT250材质与活塞环配磨的总磨损量为2.66μm,明显低于普通HT250缸体的3.15μm,略低于缸套材质的2.71μm。改性
[Abstract]:The material of cylinder block without cylinder liner can not meet the design requirement of wear resistance, so it has to insert thin-walled cylinder liner into cylinder hole. The rigidity and wear resistance of HT250 were strengthened by adding micro modified sic _ p. The effect was verified by friction and wear test, cylinder hole deformation test and bench test. The results show that the total wear of HT250 material and piston ring is 2.66 渭 m, which is lower than that of ordinary HT250 cylinder block (3.15 渭 m) and slightly lower than that of cylinder liner material (2.71 渭 m). Modification
【作者单位】： 大连交通大学材料科学与工程学院;广西玉柴机器股份有限公司;
【分类号】：TG251

【相似文献】

相关期刊论文 前10条

1 孙先荣;;气缸体堵盖压装机[J];汽车工艺;1990年03期

2 于远清;气缸体挖槽机[J];汽车技术;1974年01期

3 汪觉生;气缸体加工中偏心补偿定位销的原理和应用[J];组合机床;1980年07期

4 靳保岑;气缸体裂纹的氧—乙炔冷焊修复[J];工程机械;1982年01期

5 吴济奎;;铸铝合金气缸体松孔镀铬[J];机械工人;1985年05期

6 王恩伟;;气缸体主轴承孔以铰代珩工艺研究[J];汽车工艺;1988年06期

7 秦永排;;斯太尔气缸体机加工工艺[J];汽车工艺与材料;1992年12期

8 韦公远;修复气缸体、气缸盖裂纹的几种方法[J];机械工人.冷加工;2005年03期

9 齐建;;蓝擎气缸体铸件裂纹缺陷解决措施探讨[J];中国铸造装备与技术;2011年04期

10 ;加工两种气缸体的可调流水线[J];国外组合机床;1970年S3期

相关会议论文 前5条

1 刘文川;王兴平;范仲根;邓鑫;韩君华;汪萍;祝举章;;康明斯6BT气缸体的铸造[A];第六届21省（市、自治区）4市铸造学术会议论文集[C];2004年

2 周沭;;关于冷铁与铬矿砂在气缸体类铸件中的探索与应用[A];2013(第23届)重庆市铸造年会论文集[C];2013年

3 张明;迟建国;曹炜;樊舸;;浅谈WD/WP气缸体铸造工艺持续改进[A];2012(第22届)重庆市铸造年会论文集[C];2012年

4 王亮;刘国民;王明宇;刘垂相;;离心缸套工艺及其经济效益[A];重庆市机械工程学会铸造分会、重庆铸造行业协会2010重庆市铸造年会论文集[C];2010年

5 高护生;王金刚;樊玉光;陈朝达;陈朝进;崔自成;刘建新;;高压泵缸套失效分析与防止措施[A];第二届全国青年摩擦学学术会议论文专辑[C];1993年

相关重要报纸文章 前2条

1 潘志军;锡柴气缸体新工艺应用获成功[N];中国物资报;2000年

2 潘志军;锡柴气缸体结合面铣拉工艺应用获成功[N];中国机电日报;2000年

相关硕士学位论文 前1条

1 孙红辉;气缸体的焊接工艺与焊接变形控制研究[D];江苏科技大学;2010年

，

本文编号：2108004