2397合金高周疲劳性能及裂纹萌生扩展行为

发布时间：2018-07-16 21:36

【摘要】：研究了2397-T87铝锂合金的高周疲劳性能及裂纹萌生扩展行为。结果表明:在应力比R=0.1时,2397-T87铝锂合金L方向、LT方向和ST方向光滑试样(K_t=1.0)的疲劳寿命极限分别约为192,243和151 MPa;缺口试样(K_t=3.0)的疲劳寿命极限分别约为72,78和70 MPa。其疲劳裂纹主要萌生于试样表面,以及氧化物、夹杂等脱落形成的空洞,Al(CuFeMn)第二相杂质粒子。驻留滑移带(PSB)和晶粒取向对其疲劳裂纹早期扩展有重要影响。
[Abstract]:The high cycle fatigue properties and crack initiation propagation behavior of 2397-T87 Al-Li alloy were studied. The results show that the fatigue life limits of the L direction and St direction smooth specimens of Al-Li alloy R = 0.1 are about 192243 MPa and 151MPa, respectively, and the fatigue life limits of notched specimens (KTN 3.0) are about 72 78 and 70 MPA, respectively. The fatigue crack mainly originates on the surface of the specimen, and the second phase impurity particles of Al (CuFeMn) formed by the exfoliation of oxide and inclusions. The presence slip band (PSB) and grain orientation have important effects on the early growth of fatigue crack.
【作者单位】： 中南大学有色金属材料科学与工程教育部重点实验室;
【基金】：国家重点基础研究发展规划(“973”计划)(2012CB619503)
【分类号】：TG146.21

【相似文献】

相关期刊论文 前10条

1 韩光炜，宋余九;慢加载条件下氢对裂纹萌生与扩展的作用[J];金属学报;1994年10期

2 梅冰,李友国,汪长安,窦鹏;中碳贝氏体钢滚动接触疲劳的裂纹萌生[J];清华大学学报(自然科学版);2002年12期

3 段兴旺;刘建生;郑晓华;黑志刚;;316LN钢裂纹萌生的临界损伤值[J];塑性工程学报;2013年03期

4 鲁连涛;盐泽和章;;高速工具钢的超长寿命S-N曲线特征和内部裂纹萌生行为[J];机械工程学报;2006年12期

5 宋虎;王爱琴;李继文;;A356合金原位拉伸裂纹萌生与扩展行为分析[J];热加工工艺;2010年06期

6 朱晓锋;陆永浩;杨海波;;相界面对核电Z3CN20-09M不锈钢裂纹萌生和扩展的影响[J];材料科学与工艺;2013年05期

7 郑贤淑,李治,金俊泽;基于凝固进程数值模拟的铸件裂纹预测方法[J];材料研究学报;2000年S1期

8 杜洪奎;潘家祯;;低合金钢微缺陷的裂纹萌生扩展规律[J];机械工程材料;2008年02期

9 张纪奎;郦正能;;钛合金结构疲劳全寿命计算方法研究[J];机械强度;2010年03期

10 鄢文彬,涂铭旌;结构钢在低温下冲击断裂时的裂纹萌生与扩展[J];西安交通大学学报;1981年06期

相关硕士学位论文 前1条

1 张文;含埋藏球型缺陷管道蠕变裂纹萌生的预测[D];天津大学;2015年

，

本文编号：2127735