行波磁场对ZL205A合金元素分布的影响

发布时间：2018-07-29 20:40

【摘要】：将行波磁场作用于ZL205A合金凝固过程中,研究了不同励磁电流强度的行波磁场对ZL205A合金试样中Cu元素分布、凝固组织以及晶粒尺寸的影响。结果表明,对ZL205A合金凝固过程中施加行波磁场,合金中Cu元素分布更均匀,细化相颗粒形成的明显沉积层厚度减小,且随着励磁电流强度的增加沉积层厚度逐渐减小,直至消失。经分析,这是由于行波磁场促进细化相颗粒向试样其他位置移动,避免其在底部沉积,同时提高了试样上部的形核率,减小了试样上部的晶粒尺寸。
[Abstract]:The effect of traveling wave magnetic field on Cu distribution, solidification microstructure and grain size of ZL205A alloy was studied. The results show that when the traveling wave magnetic field is applied to the solidification process of ZL205A alloy, the distribution of Cu element in the alloy is more uniform, and the obvious thickness of deposit layer formed by fine phase particles decreases, and the thickness of deposit layer decreases gradually with the increase of excitation current intensity. Until it disappears. The analysis shows that the traveling wave magnetic field can promote the fine phase particles to move to other positions of the sample to avoid the deposition at the bottom and increase the nucleation rate of the upper part of the sample and reduce the grain size of the upper part of the sample.
【作者单位】： 中国航发北京航空材料研究院;哈尔滨工业大学材料科学与工程学院;
【分类号】：TG146.21;TG292

【相似文献】

相关期刊论文 前10条

1 吕国伟;苏彦庆;毕维生;郭景杰;;行波磁场铸造表面粗糙缺陷的成因与控制[J];铸造技术;2011年11期

2 吕国伟;苏彦庆;毕维生;郭景杰;;铸造用行波磁场分布规律的研究[J];铸造技术;2009年05期

3 徐严谨;苏彦庆;骆良顺;李新中;刘江平;郭景杰;陈瑞润;傅恒志;;行波磁场作用对凝固过程中气泡的影响(英文)[J];Transactions of Nonferrous Metals Society of China;2011年09期

4 王晓东,李廷举,金俊泽;永磁驱动的行波磁场理论及对凝固组织微细化作用[J];稀有金属材料与工程;2002年01期

5 王芳;李宝宽;沈峰满;;行波磁场作用下金属液体运动行为的数值模拟[J];东北大学学报(自然科学版);2009年08期

6 吕国伟;于波;苏彦庆;毕维生;郭景杰;;铸造用行波磁场ANSYS有限元分析[J];铸造设备研究;2008年06期

7 赵春晖;李丘林;刘伟;;利用行波磁场的驱动流去除液态铝合金中的夹杂物(英文)[J];稀有金属材料与工程;2012年S2期

8 吕国伟;苏彦庆;毕维生;郭景杰;;薄壁铝合金件行波磁场铸造的缺陷分析及控制[J];铸造技术;2010年12期

9 钟云波,任忠鸣,邓康,俞迅捷,蒋国昌,徐匡迪;行波磁场净化液态金属的电磁力参数[J];中国有色金属学报;1999年03期

10 梅振乾;电磁流槽浇铸——介绍一种新型浇铸装置[J];轻合金加工技术;1985年01期

相关博士学位论文 前2条

1 范学q，

本文编号：2153948