AZ31镁合金表面聚多巴胺膜的一步制备及腐蚀行为研究

发布时间：2018-08-07 06:46

【摘要】：利用简单的一步浸渍沉积,直接在AZ31镁合金表面制备了聚多巴胺膜层。用扫描电镜(SEM)和原子力显微镜(AFM)观察了膜层的形貌,用X射线光电子谱(XPS)对膜层成分进行了分析,用动电位极化曲线对膜层的腐蚀行为进行了研究,并通过胶带实验对膜层与基体的结合性能进行考察。结果表明,通过调整实验参数,经一步浸渍法能在镁合金表面制备完整的聚多巴胺膜层,膜层与AZ31镁合金基体结合良好,在SBF溶液中能提高镁合金的耐蚀性能。
[Abstract]:Poly (dopamine) film was prepared on AZ31 magnesium alloy surface by simple one step impregnation deposition. The morphology of the film was observed by scanning electron microscope (SEM) and atomic force microscope (AFM). The composition of the film was analyzed by X-ray photoelectron spectroscopy (XPS). The corrosion behavior of the film was studied by potentiodynamic polarization curve. The adhesive properties of the film and matrix were investigated by tape test. The results show that, by adjusting the experimental parameters, a complete polydopamine film can be prepared on the surface of magnesium alloy by one step impregnation method. The film can bind well to the substrate of AZ31 magnesium alloy, and the corrosion resistance of magnesium alloy can be improved in SBF solution.
【作者单位】： 太原理工大学材料科学与工程学院;
【基金】：山西省基础研究计划项目~~
【分类号】：TG174.46

【相似文献】

相关期刊论文 前3条

1 杜贤昌;郭淑兰;董文;徐学东;;AZ31B镁合金A-TIG单一活性剂的设计与研究[J];热加工工艺;2014年09期

2 杜九汪;王强;;AZ80镁合金带内筋薄壁壳体挤压新方法[J];轻合金加工技术;2014年05期

3 刘蒙恩;白莉;袁苗达;樊艳丽;;AZ31镁合金/AgCu合金/5083铝合金TLP扩散焊研究[J];热加工工艺;2014年09期

相关博士学位论文 前3条

1 申Pr伯;生物活性涂层包覆镁合金的制备与性能研究[D];天津大学;2016年

2 高蕊;镁合金表面超疏水膜层构筑及其防腐性能研究[D];哈尔滨工程大学;2014年

3 张玉芬;镁合金表面超疏水涂层的构建及其腐蚀行为[D];哈尔滨工业大学;2017年

相关硕士学位论文 前8条

1 朱弋;脉冲强磁场处理AZ31镁合金的微观组织和力学性能研究[D];江苏大学;2017年

2 张敏;镁合金表面植酸/羟基磷灰石生物活性涂层的制备及性能研究[D];天津大学;2016年

3 刘耿;新型全降解镁合金气管支架的制备及性能评价[D];郑州大学;2017年

4 顾佳炜;镁合金表面镍基非晶态镀层制备工艺及其耐蚀性研究[D];西安科技大学;2017年

5 张佳斌;Ca和Ce/La在镁合金中的协同强化机制及其防护涂层性能的研究[D];吉林大学;2017年

6 陈杨政;Mg-xZr-ySr-zSn-0.5Ca生物镁合金组织，力学性能和腐蚀行为研究[D];江西理工大学;2017年

7 韩峗;反应扩散型镁合金钎料制备及评价[D];西安科技大学;2017年

8 刘晓庆;AZ31B/TC4异种金属TIG熔钎焊工艺及接头组织与性能研究[D];西安科技大学;2017年

，

本文编号：2169210