进口与国产轴承钢夹杂物特征的对比研究
发布时间：2018-08-18 15:55
【摘要】：为研究进口与国产高端轴承钢的夹杂物特征差异,使用ASPEX-explorer和光学显微镜分别对一种进口各向同性轴承钢和一种国产高端轴承钢的夹杂物尺寸、形态进行了多尺度评价。并使用扫描电镜对大尺寸夹杂物的元素分布进行了研究,分析了夹杂物复合化模型。结果表明,与相同生产流程的国产高端轴承钢相比,进口各向同性轴承钢夹杂物更加细小,形态椭球化,可降低各向异性;进口钢的夹杂物尺寸及形态控制均优于国产钢。进口各向同性轴承钢中大尺寸夹杂物以复合化形式出现,复合方式是以Ca S颗粒包覆刚性夹杂物,实现了夹杂物的低害化。
[Abstract]:In order to study the difference of inclusion characteristics between imported and domestic high-end bearing steels, the size and morphology of inclusions in an imported isotropic bearing steel and a domestic high-end bearing steel were evaluated by means of ASPEX-explorer and optical microscope. The results show that the inclusions of imported isotropic bearing steel are finer and the shape is ellipsoidal than that of domestic high-end bearing steel with the same production process, and the anisotropy can be reduced. Composite form appears, and the composite way is to coat rigid inclusions with Ca S particles, which realizes the low-harm of inclusions.
【作者单位】： 钢铁研究总院;
【基金】：国家自然科学基金项目资助项目(51474076) 国家国际科技合作专项资助项目(2015DFG51950)
【分类号】：TG142.1
本文编号：2189956
[Abstract]:In order to study the difference of inclusion characteristics between imported and domestic high-end bearing steels, the size and morphology of inclusions in an imported isotropic bearing steel and a domestic high-end bearing steel were evaluated by means of ASPEX-explorer and optical microscope. The results show that the inclusions of imported isotropic bearing steel are finer and the shape is ellipsoidal than that of domestic high-end bearing steel with the same production process, and the anisotropy can be reduced. Composite form appears, and the composite way is to coat rigid inclusions with Ca S particles, which realizes the low-harm of inclusions.
【作者单位】： 钢铁研究总院;
【基金】：国家自然科学基金项目资助项目(51474076) 国家国际科技合作专项资助项目(2015DFG51950)
【分类号】：TG142.1
【相似文献】
相关博士学位论文 前1条
1 李志强;GCr15轴承钢加热过程中组织演变规律的实验和模拟[D];北京科技大学;2017年
相关硕士学位论文 前6条
1 周德福;镁对H13热作模具钢组织及夹杂物的影响[D];安徽工业大学;2017年
2 李浩;镁合金化对低碳钢组织及力学性能的影响[D];安徽工业大学;2017年
3 沈千成;高标轴承钢SUJ2的质量控制研究[D];安徽工业大学;2017年
4 李远远;Ce合金化下FAB法埋弧焊缝组织与性能研究[D];江苏科技大学;2017年
5 王艳江;中碳Cr、Mo渗氮轴承钢的耐磨与疲劳性能研究[D];河北科技大学;2017年
6 张美宏;M50钢表面损伤行为和胶合失效机制分析[D];哈尔滨工业大学;2017年
，本文编号：2189956
本文链接：https://www.wllwen.com/kejilunwen/jiagonggongyi/2189956.html