基于长脉冲激光的304L不锈钢表面微织构加工

发布时间：2018-08-23 15:14

【摘要】：通过改变长脉冲激光输出功率和脉宽,在304L不锈钢表面加工出凹坑、凸包微织构,并观察了它们的形貌特征。研究结果表明,利用小脉宽、大功率激光可加工得到外形较好的凹坑,脉宽不变时,凹坑深度和直径随功率的增加呈先上升后下降的趋势。然而,大脉宽、小功率激光加工可得到外形较好的凸包,功率对凸包形貌的影响比脉宽的影响大,当功率达到一定值时,凸包高度和直径达到饱和状态。
[Abstract]:By changing the output power and pulse width of long pulse laser, pits and convexity microtextures were fabricated on the surface of 304L stainless steel, and their morphologies were observed. The results show that the pits with good shape can be obtained by using small pulse width and high power laser. When the pulse width is constant, the depth and diameter of the pits increase first and then decrease with the increase of power. However, large pulse width, low power laser processing can obtain a better shape of convex hull, the influence of power on the shape of convex hull is greater than that of pulse width. When the power reaches a certain value, the height and diameter of convex hull reach saturation state.
【作者单位】： 南京农业大学工学院;
【基金】：江苏省自然科学基金青年基金(BK20150685) 中央高校基本科研业务费(KYZ201659) 南京农业大学工学院优秀青年人才科技基金(YQ201604)
【分类号】：TG665

【相似文献】

相关期刊论文 前2条

1 秦渊;倪晓武;陈彦北;;长脉冲激光致铝合金靶产生热应力的数值研究[J];红外与激光工程;2008年S3期

2 ;[J];;年期

相关会议论文 前1条

1 秦渊;倪晓武;陈彦北;;长脉冲激光致铝合金靶产生热应力的数值研究[A];2008年激光探测、制导与对抗技术研讨会论文集[C];2008年

相关硕士学位论文 前8条

1 王洋;长脉冲激光与金属相互作用分析[D];长春理工大学;2008年

2 窦如凤;长脉冲激光致介质薄膜损伤机理与阈值测量研究[D];南京理工大学;2009年

3 张一鸣;长脉冲激光致金属熔融喷溅的理论研究[D];南京理工大学;2013年

4 付耀龙;长脉冲激光辐照硅材料的损伤研究[D];长春理工大学;2013年

5 张梁;长脉冲激光与半导体材料的热作用的数值分析[D];南京理工大学;2007年

6 范子嘉;长脉冲激光与金属相互作用的热分析[D];长春理工大学;2010年

7 李政;重复频率长脉冲激光作用光学玻璃的热特性研究[D];长春理工大学;2013年

8 王冰;长脉冲激光辐照金属铝LY12的温度场与应力场研究[D];长春理工大学;2014年

，

本文编号：2199450