铁塔用Q420B大规格角钢的组织与性能研究
发布时间：2018-08-28 17:34
【摘要】：采用光学显微镜、扫描电镜、拉伸试验和冲击试验等方法研究了铁塔用Q420B大规格角钢的组织和性能。结果表明,Q420B角钢组织为铁素体+珠光体,晶粒尺寸细小、均匀。3种不同肢厚25~#Q420B角钢的屈服强度为471~496 MPa,抗拉强度为617~627 MPa,伸长率为23%~29%,冲击韧性均达到国家标准规定的D级。
[Abstract]:The microstructure and properties of Q420B angle steel for iron tower were studied by means of optical microscope, scanning electron microscope, tensile test and impact test. The results show that the microstructure of Q420B angle steel is ferrite + pearlite with fine grain size and uniformity. The length is 23%~29%, and the impact toughness is up to D grade stipulated by the national standard.
【作者单位】： 华北理工大学冶金与能源学院;唐山钢铁有限公司技术中心;
【基金】：国家自然科学基金资助项目(51474092) 河北省高等学校创新团队领军人才培育计划(LJRC007) 河北省科技厅资助项目(E2013209228、12212122D) 唐山市科技计划资助项目(14110201A)
【分类号】：TG142.1
本文编号：2210089
[Abstract]:The microstructure and properties of Q420B angle steel for iron tower were studied by means of optical microscope, scanning electron microscope, tensile test and impact test. The results show that the microstructure of Q420B angle steel is ferrite + pearlite with fine grain size and uniformity. The length is 23%~29%, and the impact toughness is up to D grade stipulated by the national standard.
【作者单位】： 华北理工大学冶金与能源学院;唐山钢铁有限公司技术中心;
【基金】：国家自然科学基金资助项目(51474092) 河北省高等学校创新团队领军人才培育计划(LJRC007) 河北省科技厅资助项目(E2013209228、12212122D) 唐山市科技计划资助项目(14110201A)
【分类号】：TG142.1
【相似文献】
相关期刊论文 前2条
1 王德宝;王越;陈联满;崔磊;;Q420B角钢腿部裂纹形态分析及成因探讨[J];轧钢;2010年01期
2 ;[J];;年期
相关会议论文 前1条
1 李永祥;李斌;张杰新;;Q420B角钢钒氮微合金化工艺研究与开发[A];2012年全国炼钢—连铸生产技术会论文集（上）[C];2012年
，本文编号：2210089
本文链接：https://www.wllwen.com/kejilunwen/jiagonggongyi/2210089.html