不同热输入下基于MCJNi1K焊丝的Q460E钢埋弧焊缝组织性能研究

发布时间：2018-09-05 19:38

【摘要】：使用自主研制的MCJNi1K低碳中锰高硅焊丝对Q460E低合金高强钢进行埋弧焊接试验,对不同热输入条件下焊缝金属的组织和性能进行了研究。结果表明,在一定的范围内随热输入增大,焊缝金属低温冲击韧性先增大再降低。当热输入为21.92 k J/cm时,低温冲击韧性最高,焊缝区随组织主要为针状铁素体,断口有韧窝特征。热输入较小或较大时,焊缝区分别有先共析铁素体和魏氏组织产生,均会降低低温冲击韧性。
[Abstract]:The submerged arc welding test of Q460E low alloy high strength steel was carried out using MCJNi1K low carbon medium manganese high silicon welding wire. The microstructure and properties of weld metal under different thermal input conditions were studied. The results show that the low temperature impact toughness of weld metal increases first and then decreases with the increase of heat input in a certain range. When the heat input is 21.92k J/cm, the low temperature impact toughness is the highest, the weld zone is mainly acicular ferrite with microstructure, and the fracture has dimple characteristics. When the heat input is small or large, there are preeutectoid ferrite and Weiss microstructure in the weld zone, which can reduce the impact toughness at low temperature.
【作者单位】： 武汉理工大学材料科学与工程学院;
【分类号】：TG457.11

【相似文献】

相关期刊论文 前10条

1 李廷忠;吴圣川;;等离子熔积成形热输入数学模型研究[J];电焊机;2006年06期

2 罗爱辉;张延松;陈关龙;朱文峰;;基于有限元法的电阻点焊电极热输入机理[J];焊接学报;2008年05期

3 及玉梅;付魁军;徐光;翟晓莉;;船板生产工艺对高热输入焊接性能影响的对比与分析[J];焊接;2007年05期

4 俞海良;芦凤桂;苏冬梅;裴培;姚舜;;热输入对焊缝金属组织性能影响的预测及试验研究[J];焊接技术;2008年02期

5 张德勤,田志凌,杜则裕,云绍辉;热输入对X65钢焊缝金属组织及性能的影响[J];焊接学报;2001年05期

6 夏佃秀;尚成嘉;孙卫华;侯东华;陈晔;;低合金高强钢大热输入焊接热影响区组织性能[J];焊接学报;2011年04期

7 娄宇航;肖红军;田志凌;彭增华;;热输入对E40钢双丝埋弧焊焊缝组织及性能的影响[J];材料科学与工艺;2013年01期

8 丁福保,马玉江,陈一清;不同热输入的低合金钢HAZ中组织、夹杂对韧性的影响[J];焊接学报;1984年04期

9 于华,张柯柯,陈天杰,崔慧君;热输入对A517、A537钢冲击性能的影响[J];热加工工艺;2005年05期

10 张婷婷;王文先;闫志峰;王志斌;张心保;;热输入对445J2超纯铁素体不锈钢焊接接头显微组织和力学性能的影响[J];太原理工大学学报;2014年02期

相关重要报纸文章 前1条

1 ;大热输入焊接用中厚板生产技术[N];世界金属导报;2012年

相关博士学位论文 前3条

1 石明浩;微锆钢大热输入焊接热影响区性能及组织演变规律的研究[D];东北大学;2014年

2 张朋彦;大热输入焊接用钢的制造工艺及其产业化技术研究[D];东北大学;2011年

3 阿荣;大热输入钢焊缝组织及韧性改善[D];钢铁研究总院;2014年

相关硕士学位论文 前1条

1 娄宇航;E40钢大热输入焊接接头组织与性能研究[D];昆明理工大学;2012年

，

本文编号：2225267