TC4“一脉一孔”PAW工艺研究

发布时间：2018-10-04 22:41

【摘要】：采用直流穿孔型PAW和"一脉一孔"型PAW焊接工艺进行了3 mm和6 mm厚TC4焊接试验,并对焊接试板外观、内部缺欠、机械性能及工艺性能进行了测试。结果显示,两种焊接方法焊接接头质量均能满足标准要求,但"一脉一孔"型PAW在降低气孔、降低焊缝下凹方面效果更好;对于中薄型钛及钛合金的等离子弧焊接,"一脉一孔"型PAW效果更好。
[Abstract]:The welding tests of 3 mm and 6 mm thick TC4 were carried out with DC perforated PAW and "one pulse and one hole" PAW welding process. The appearance, internal defects, mechanical properties and technological properties of the welding test plate were tested. The results show that the quality of the two welding methods can meet the standard requirements, but the "one pulse, one hole" type PAW is more effective in reducing the porosity and the lower pit of the weld. For medium-thin titanium and titanium alloy plasma arc welding, "one pulse, one hole" type PAW is better.
【作者单位】： 中国船舶重工集团公司第七二五研究所;
【基金】：国家自然科学基金(U1404502)
【分类号】：TG456.2

【相似文献】

相关期刊论文 前10条

1 张云霞;马铁军;张勇;杨思乾;;TC4直流点焊电流波形的频谱与熔核直径的关系[J];电焊机;2008年05期

2 马铁军;杨思乾;张勇;李文亚;;TC4线性摩擦焊接头的力学性能及组织变化特点[J];焊接学报;2007年10期

3 温爱玲;闫秀侠;任瑞铭;王生武;;高能喷丸时间对TC4疲劳性能的影响[J];热加工工艺;2009年14期

4 谢英杰;席锦会;曲恒磊;邓超;;大规格TC4铸锭真空自耗电弧熔炼控制方式对比[J];热加工工艺;2010年19期

5 陈恳;超塑用 TC4 钛合金板材在某型飞机上的应用[J];航空制造工程;1997年12期

6 许海鹰;曹子文;邹世坤;车志刚;;激光冲击处理对TC4氩弧焊焊缝力学性能的影响[J];稀有金属材料与工程;2012年04期

7 曲伸;;电子束焊接TC4整体叶盘结构的变形控制[J];航空制造技术;2009年23期

8 张霜银;林鑫;陈静;黄卫东;;热处理对激光立体成形TC4残余应力的影响[J];稀有金属材料与工程;2009年05期

9 王学德;李启鹏;周鑫;仝崇楼;胡雅骥;;激光冲击强化提高TC4叶片振动疲劳性能[J];中国表面工程;2012年02期

10 黄云峰;;TC4马蹄形接头等温锻造成形工艺数值模拟研究[J];热加工工艺;2012年13期

相关会议论文 前3条

1 雷强;吴辉;李文亚;马铁军;;母材组织对TC4线性摩擦焊接头组织与拉伸性能影响[A];第十五次全国焊接学术会议论文集[C];2010年

2 张云霞;马铁军;张勇;杨思乾;;分流条件下TC4直流点焊电流波形的频谱与熔核直径的关系[A];陕西省焊接学术会议论文集[C];2006年

3 王永哲;张鹏;田琳;;热处理制度对TC4小棒材组织和性能的影响[A];第十四届全国钛及钛合金学术交流会论文集（下册）[C];2010年

相关博士学位论文 前1条

1 范国强;TC4板材局部自阻电加热数控渐进成形的研究[D];南京航空航天大学;2010年

相关硕士学位论文 前1条

1 包珍强;缺口对TC4高循环疲劳强度的影响及预测方法研究[D];南京航空航天大学;2014年

，

本文编号：2252155