AZ61和AZ91镁合金在不同浓度NaCl溶液中的腐蚀特性

发布时间：2018-10-17 08:19

【摘要】：采用失重法和扫描电镜法研究了AZ61与AZ91镁合金在不同浓度Na Cl溶液中的腐蚀特性,Na Cl溶液的浓度分别为0.001,0.01,0.1,0.2和0.3mol/L。实验结果表明,在Na Cl溶液的浸泡实验中,在相同的浸泡时间(5d)下,Na Cl溶液浓度增大,AZ61和AZ91镁合金的腐蚀速率增大,腐蚀程度增强,抗腐蚀性减弱。在相同浓度的Na Cl溶液中浸泡相同时间(5d)的情况下,AZ61镁合金的抗腐蚀性较好,AZ91镁合金较差。
[Abstract]:The corrosion characteristics of AZ61 and AZ91 magnesium alloys in Na Cl solution with different concentration were studied by weight loss method and scanning electron microscope. The concentration of, Na Cl solution was 0.001g / L and 0.3mol / L, respectively. The experimental results show that the corrosion rate of AZ61 and AZ91 magnesium alloys increases, the corrosion degree increases and the corrosion resistance weakens when the concentration of, Na Cl solution increases under the same immersion time (5 days) in Na Cl solution. The corrosion resistance of AZ61 magnesium alloy was better than that of AZ91 magnesium alloy when immersed in the same concentration of Na Cl solution for the same time (5 d).
【作者单位】： 吕梁学院化学化工系;
【基金】：吕梁学院校内青年基金,AZ系列镁合金在不同环境下的腐蚀机理研究(ZRQN201502);吕梁学院校内青年基金,时效处理制度对经济型双相不锈钢2012腐蚀性能的影响研究(ZRQN201501)
【分类号】：TG146.22

【相似文献】

相关期刊论文 前7条

1 张丁非;耿青梅;杨绪盛;余大亮;潘复生;;新型复合挤压工艺中温度对AZ61组织和性能的影响[J];材料工程;2014年07期

2 严楷;李元东;马颖;陈体军;;熔体处理温度对自孕育法制备AZ61半固态浆料的影响[J];特种铸造及有色合金;2011年05期

3 陈国平;周天瑞;闫洪;张发云;刘宏;;半固态镁合金AZ61压缩变形力学行为的研究[J];铸造技术;2007年08期

4 周冰锋;闫洪;;试验研究半固态AZ61合金的本构关系[J];中国机械工程;2006年17期

5 胡志;闫洪;凌李石保;聂俏;刘少平;;纳米SiC颗粒增强AZ61镁基复合材料制备工艺的优化[J];铸造;2009年09期

6 彭建;周绸;陶健全;潘复生;;AZ31与AZ61异种镁合金的TIG焊研究[J];材料工程;2011年02期

7 ;[J];;年期

相关会议论文 前1条

1 周冰锋;闫洪;;应用回归方法建立半固态AZ61合金的本构关系[A];第三届华东六省一市塑性工程学术年会论文集[C];2005年

相关硕士学位论文 前1条

1 王晨;镁合金AZ61热变形特性及锥齿轮热锻成形研究[D];上海交通大学;2012年

，

本文编号：2276067