可降解医用镁合金在骨修复应用中的研究进展

发布时间：2018-10-19 14:50

【摘要】：镁合金可在人体内完全降解,其弹性模量与人皮质骨接近,可有效避免应力遮挡效应,且具有较高的机械强度和良好的骨诱导性,因此镁合金作为骨修复材料具有很好的应用潜力,并受到广泛研究。本文对可降解医用镁合金材料在骨修复领域的研究进行了总结,分别从镁合金骨修复材料的优势,发展历史,存在的问题与挑战,近几年的研究进展等几个方面进行了阐述。文章最后介绍了上海交通大学轻合金精密成型国家工程研究中心团队在骨修复用镁合金方面的最新研究成果,以及为推动我国可降解医用镁合金的产业化进程方面所做的工作。
[Abstract]:Magnesium alloy can be completely degraded in human body, and its elastic modulus is close to that of human cortical bone, which can effectively avoid stress shielding effect, and has high mechanical strength and good bone inductivity. Therefore, magnesium alloys as bone repair materials have good application potential, and are widely studied. In this paper, the research on biodegradable medical magnesium alloy materials in the field of bone repair is summarized. The advantages, development history, existing problems and challenges of magnesium alloy bone repair materials, and the research progress in recent years are described respectively. In the end, the paper introduces the latest research results of the national engineering research center of light alloy precision molding of Shanghai Jiaotong University in the field of magnesium alloy for bone repair, and the work done to promote the industrialization of degradable medical magnesium alloy in China.
【作者单位】： 上海交通大学轻合金精密成型国家工程研究中心和金属基复合材料国家重点实验室;沪创医疗科技(上海)有限公司;
【基金】：国家高技术研究发展计划项目No.2015AA033603 国家自然科学基金项目No.51571143 上海市科委企业国际合作项目No.17440730700 2017年度上海市优秀学术带头人计划No.17XD1402100~~
【分类号】：R318.08;TG146.22

【相似文献】

相关期刊论文 前3条

1 杜贤昌;郭淑兰;董文;徐学东;;AZ31B镁合金A-TIG单一活性剂的设计与研究[J];热加工工艺;2014年09期

2 杜九汪;王强;;AZ80镁合金带内筋薄壁壳体挤压新方法[J];轻合金加工技术;2014年05期

3 刘蒙恩;白莉;袁苗达;樊艳丽;;AZ31镁合金/AgCu合金/5083铝合金TLP扩散焊研究[J];热加工工艺;2014年09期

相关博士学位论文 前2条

1 申Pr伯;生物活性涂层包覆镁合金的制备与性能研究[D];天津大学;2016年

2 高蕊;镁合金表面超疏水膜层构筑及其防腐性能研究[D];哈尔滨工程大学;2014年

相关硕士学位论文 前3条

1 张敏;镁合金表面植酸/羟基磷灰石生物活性涂层的制备及性能研究[D];天津大学;2016年

2 刘耿;新型全降解镁合金气管支架的制备及性能评价[D];郑州大学;2017年

3 杨潇然;新型骨植入镁合金组织和降解产物及其生物相容性评价[D];郑州大学;2017年

，

本文编号：2281462