激光焊接工艺对GH188合金焊缝成形及力学性能的影响

发布时间：2018-11-02 08:42

【摘要】：研究了激光焊接工艺对GH188合金焊接接头焊缝成形及力学性能的影响。结果表明,高激光功率或低焊接速度对GH188合金焊缝成形不利,使焊缝背面存在飞溅和轻微咬边现象,接头焊缝区晶粒粗大且接头抗拉强度低。随着焊接速度的增大,焊缝宽度减小,焊缝背面飞溅减少;随着激光功率的增大,焊缝宽度增加,焊缝背面飞溅增多。当激光功率为2.83.2kW、焊接速度为6m/min时,焊缝成形和接头拉伸性能均较好。
[Abstract]:The effect of laser welding process on weld formation and mechanical properties of GH188 alloy welded joint was studied. The results show that high laser power or low welding speed is unfavorable to the weld formation of GH188 alloy, resulting in spatter and slight edging on the back of the weld, the grain size in the weld zone of the joint is coarse and the tensile strength of the joint is low. With the increase of the welding speed, the width of the weld decreases and the spatter on the back of the weld decreases, and with the increase of laser power, the width of the weld increases and the spatter on the back of the weld increases. When the laser power is 2.83.2kW and the welding speed is 6m/min, the weld forming and tensile properties of the joints are better.
【作者单位】： 中航工业北京航空制造工程研究所高能束流加工技术重点实验室;
【分类号】：TG456.7

【相似文献】

相关期刊论文 前10条

1 姚伟,巩水利,陈俐;钛合金激光穿透焊的焊缝成形(Ⅱ)[J];焊接学报;2004年05期

2 王博;;混合保护气体成分对不锈钢气保焊焊缝成形的影响[J];价值工程;2012年10期

3 许先果;熊跃;;混合保护气体成分对焊缝成形的影响[J];焊接技术;1990年06期

4 焦向东，潘际銮，张骅;AC／DCRP交替MIG焊接方法的研究[J];中国机械工程;1996年02期

5 石永华;林水强;郑泽培;;水下湿法焊缝成形的响应曲面法建模及分析[J];焊接学报;2014年04期

6 高燕,韩国明,李建强;不锈钢激光焊焊缝成形的数学模型[J];电焊机;2005年10期

7 蒋凡;陈树君;王龙;于洋;;焊枪行走角变化对等离子弧穿孔立焊焊缝成形的影响规律[J];焊接学报;2013年02期

8 王爱珍,王志新,安秀清;焊接规范对压力管道焊缝成形质量的影响[J];河南科技;1998年02期

9 石永华;郑泽培;黄晋;;水下湿法药芯焊丝焊接焊缝成形预测的敏感度模型(英文)[J];Transactions of Nonferrous Metals Society of China;2013年07期

10 雷玉成;铝合金等离子弧立焊焊缝成形稳定性的研究[J];焊接技术;1994年03期

相关会议论文 前6条

1 刘凤德;张宏;王宇琪;;热源间距对激光-电弧复合焊焊缝成形和组织的影响[A];第十六次全国焊接学术会议论文摘要集[C];2011年

2 张林杰;张建勋;曹伟杰;柴国明;巩水利;;工艺参数对304不锈钢脉冲Nd:YAG激光/TIG电弧复合焊焊缝成形的影响[A];第十五次全国焊接学术会议论文集[C];2010年

3 许飞;巩水利;杨t，

本文编号：2305515