铸造技术路线图:半固态铸造

发布时间：2018-11-04 16:46

【摘要】：正第一节概述半固态铸造技术是将含有非枝晶固相的固液金属混合物在凝固温度范围内加工成形的一种金属材料成形技术~([1])。与传统金属材料成形方法相比,半固态铸造技术具有如下特点:(1)被加工的材料处于液固共存两相区,一方面,可减少凝固潜热和凝固收缩,有利于实现更精确的近终成形;另一方面,由于成形温度低,减轻了模具的热冲击,提高模具的使用寿命,同时减少了零件凝固时间,提高了零件的成形速度。(2)半固
[Abstract]:In the first section, the semisolid casting technology is introduced. It is a kind of metal material forming technology which is used to form solid liquid metal mixture containing non-dendritic solid phase in the range of solidification temperature. Compared with the traditional metal material forming method, the semi-solid casting technology has the following characteristics: (1) the processed material is in the liquid-solid coexistence two-phase zone, on the one hand, it can reduce the solidification latent heat and solidification shrinkage. It is advantageous to realize more accurate near end forming; On the other hand, because of the low forming temperature, the thermal shock of the die is alleviated, the service life of the die is increased, and the solidification time of the part is reduced, and the forming speed of the part is improved. (2) Semi-solid.
【分类号】：TG249.9

【相似文献】

相关期刊论文 前10条

1 贾玉贤,王承志,黄勇,李玉海;半固态铸造技术的现状及发展趋势[J];铸造设备研究;2003年05期

2 刘汾;金属半固态铸造技术及其应用前景[J];太原科技;2004年05期

3 赵大志,路贵民,崔建忠;半固态铸造技术的发展状况及前景[J];铸造;2005年10期

4 潘志勇;;半固态铸造工艺简介[J];湖南工业职业技术学院学报;2006年04期

5 李响;付云鹏;;半固态铸造的现状及发展前景[J];科技传播;2012年24期

6 仇庆根;半固态铸造的一次固态颗粒成因分析[J];浙江工学院学报;1983年01期

7 苏华钦 ,朱鸣芳,高志强;半固态铸造的现状及发展前景[J];特种铸造及有色合金;2002年S1期

8 印飞 ,王亦新,洪慎章,曾振鹏;半固态铸造铝合金材料的研究现状[J];特种铸造及有色合金;2002年S1期

9 符寒光;半固态铸造技术研究现状与展望[J];冶金信息导刊;2002年05期

10 梁志明,符寒光;半固态铸造技术研究现状与展望[J];铸造设备研究;2002年06期

相关会议论文 前1条

1 苏华钦;胡彬;;国内外半固态铸造的工业应用现状及面临的机遇与对策[A];中国铸造行业第五届高层论坛论文集[C];2011年

相关重要报纸文章 前1条

1 苏鸿英;镁合金半固态铸造技术开发现状[N];中国有色金属报;2004年

，

本文编号：2310495