Cr合金化对Fe-36Ni因瓦合金性能的影响

发布时间：2019-01-26 11:40

【摘要】：通过Thermo-Calc热力学计算、热膨胀系数检测、金相分析以及硬度检测,研究了Cr含量对Fe-36Ni因瓦合金性能的影响。结果表明:添加Cr元素后,合金基体仍为单一奥氏体组织,Cr的加入未破坏因瓦合金的稳定性。随Cr元素含量增加,合金的热膨胀系数提高,平均晶粒尺寸由65.4μm逐渐下降至34.4μm,硬度由150.7 HV2逐渐升高至169.9 HV2,合金化效果明显。
[Abstract]:The effect of Cr content on the properties of Fe-36Ni Intile alloy was studied by means of Thermo-Calc thermodynamic calculation, thermal expansion coefficient test, metallographic analysis and hardness test. The results show that the alloy matrix is still a single austenitic structure after the addition of Cr element, and the addition of Cr does not destroy the stability of the Inwar alloy. With the increase of Cr content, the thermal expansion coefficient of the alloy increases, the average grain size decreases from 65.4 渭 m to 34.4 渭 m, and the hardness increases from 150.7 HV2 to 169.9 HV2,.
【作者单位】： 北京科技大学冶金与生态工程学院;中国联合工程公司;
【基金】：国家自然科学基金(51674020)
【分类号】：TG142.1

【相似文献】

相关期刊论文 前10条

1 陈昀;李明光;张艳红;张明霞;;因瓦合金发展现状及应用前景[J];机械研究与应用;2009年04期

2 ;可变形因瓦合金36H的热处理[J];金属功能材料;1996年05期

3 ;因瓦合金的成分和热处理对其性能的影响[J];金属功能材料;1999年02期

4 启明;高强度因瓦合金[J];金属功能材料;2001年01期

5 朱振华;高强度因瓦合金[J];机械工程材料;1983年04期

6 李青禄;胡笛川;;因瓦合金的特性及应用前景[J];机械管理开发;2007年06期

7 卢琳;刘天成;李鹏;章愫;;电沉积因瓦合金镀层成分的影响因素[J];北京科技大学学报;2008年08期

8 骆良顺;张宇民;张凤海;苏彦庆;李琨;陈大勇;郭景杰;傅恒志;;微量钴合金化的因瓦合金模具铸造成形试验研究[J];铸造;2010年10期

9 徐培全;马春伟;金玲玮;黄晨;何建萍;;高黏结相硬质合金与因瓦合金焊接组织性能[J];上海交通大学学报;2008年S1期

10 王希靖;柴廷玺;赵青山;王江;王奇;;因瓦合金4J36等离子焊接工艺及接头性能[J];焊接学报;2014年04期

相关会议论文 前2条

1 陆建生;沈黎明;;Fe-36Ni因瓦合金研究进展[A];第五届中国功能材料及其应用学术会议论文集Ⅱ[C];2004年

2 徐鹏;杨海方;顾长志;;因瓦合金纳米点接触的电阻与温度关系的研究[A];2005年纳米和表面科学与技术全国会议论文摘要集[C];2005年

相关博士学位论文 前1条

1 王超;顺磁性元素改善因瓦合金性能研究[D];西安建筑科技大学;2013年

相关硕士学位论文 前4条

1 刘洪旺;高性能因瓦合金的研究[D];河北工业大学;2015年

2 袁均平;变形及热处理对因瓦合金组织与性能的影响[D];中南大学;2005年

3 李莉娜;YG20与因瓦合金真空扩散焊接技术的研究[D];大连交通大学;2009年

4 赵宇星;钽与因瓦合金电子束焊接接头组织及工艺研究[D];哈尔滨工业大学;2014年

，

本文编号：2415442