42CrMo基体上Ni60涂层的电接触强化研究

发布时间：2019-02-14 22:44

【摘要】：采用涂刷法,将Ni60粉末均匀刷涂到42Cr Mo基体的表面形成预涂层。利用电接触表面强化技术对预涂层进行强化,获得强化层。对该强化层进行显微组织、显微硬度、相结构和抗热震性能研究。结果表明:电接触强化工艺使涂层孔隙率减少,致密性增加,同时提高了涂层的硬度和抗热震性能。
[Abstract]:The Ni60 powder was evenly brushed to the surface of 42Cr Mo substrate to form a pre-coating. The electric contact surface strengthening technique was used to strengthen the pre-coating and the strengthening layer was obtained. The microstructure, microhardness, phase structure and thermal shock resistance of the strengthened layer were studied. The results show that the porosity and densification of the coating are decreased and the hardness and thermal shock resistance of the coating are improved by the electric contact strengthening process.
【作者单位】： 东华大学机械学院纺织装备教育与研究中心;
【基金】：上海市重点学科建设资助项目(B602)
【分类号】：TG174.4

【相似文献】

相关期刊论文 前10条

1 向文才;;对电接触炉有关公式的认识[J];金属制品;1989年03期

2 楚振斌;电接触磨削实验报告[J];机床与工具;1957年12期

3 赵志明;电接触炉电压公式的探讨及对传统公式的质疑[J];金属制品;1988年02期

4 赵志明;电接触炉电压公式中有关钢丝预热温度的探讨及计算[J];金属制品;1990年01期

5 钟玉川;;电接触切割设备[J];机械设计与制造;1988年01期

6 朱振荣;新型电接触薄膜保护剂的发展[J];宇航材料工艺;1987年05期

7 胡冀远;蔡建国;;利用电接触炉生产正火钢丝[J];金属制品;1991年05期

8 陈定一;居德明;;电接触电阻加热挤(滚)压高铬铸铁的实验研究[J];安徽工学院学报;1989年01期

9 钟灿贤;弹簧钢件在水介质中电接触处理法[J];国外金属热处理;1997年01期

10 陈定一;电接触电阻加热挤压镍、铬金合铸铁[J];机床;1987年02期

相关会议论文 前1条

1 于军琪;孙龙杰;席爱民;;钢丝电接触运动加热温度的模糊神经网络控制[A];全国冶金企业计控网络化研讨会论文集[C];2003年

相关硕士学位论文 前4条

1 朱浩;42CrMo钢表面涂层制备工艺的研究[D];东华大学;2017年

2 郝晓磊;电接触强化预涂层的制备[D];东华大学;2017年

3 罗湘;高性能镍基厚涂层的制备工艺及强化[D];东华大学;2017年

4 胡祯;YSZ活性扩散障层抗热震性能的研究[D];西安建筑科技大学;2016年

，

本文编号：2422681