Ti-6246中α相转变织构的形成机制
[Abstract]:The microstructure and crystal orientation of 尾-phase forged Ti-6246 cake billet were studied by EBSD. The results show that the 尾-forged Ti-6246 alloy has a basket structure and the original 尾 grain is elongated along the flow direction of the metal. The 尾 phase exhibits a strong filament texture parallel to the compression direction of the cake billet. The texture type of the secondary 伪 phase is in accordance with the Burgers orientation relationship between the 尾 phase and the secondary 伪 phase. When the adjacent original 尾 grains have a similar 110 direction, the c-axis of the secondary 伪-phase precipitated on both sides of the 尾 / 尾 grain boundary will follow this common 110 direction, that is, the variant selection will occur. The results show that the maximum texture density of 伪 phase on {0001} polar graph is obviously higher than that of 尾 phase on (0001) polar graph.
【作者单位】： 中国科学院金属研究所;中国科学技术大学材料科学与工程学院;宝钛集团有限公司;
【分类号】：TG146.23
【相似文献】
相关期刊论文 前10条
1 楼宏青;杨豪;顾明元;童建华;;12CrNi3A钢魏氏α相形成条件及形貌的研究[J];金属热处理学报;1986年02期
2 俞学节 ,汪建林;47121β-钛合金中α相形貌对强化和断裂行为的影响[J];上海钢研;1984年02期
3 吴欢;赵永庆;葛鹏;周伟;;β稳定元素对钛合金α相强化行为的影响[J];稀有金属材料与工程;2012年05期
4 王荣;钛合金中富氧α相的鉴定与分析[J];理化检验(物理分册);2003年11期
5 王凯旋;曾卫东;赵永庆;邵一涛;周建华;王晓英;周义刚;;钛合金片层α相在热加工过程中演变规律的定量研究(英文)[J];稀有金属材料与工程;2010年04期
6 孙峰;李金山;寇宏超;唐斌;常辉;蔡建明;周廉;;Ti60钛合金α相溶解动力学及固溶组织特征[J];中国有色金属学报;2010年S1期
7 李箭,孙福玉;Fe-Mn-C系γ→α相变驱动力计算[J];钢铁研究学报;1991年01期
8 战绮明;ZCuZn40Mn3Fe1金相组织中α相含量对机械性能的影响[J];热加工工艺;1993年06期
9 孙郧立，，俞汉清，周义刚;等轴α相含量对TC11合金热稳定性的影响[J];稀有金属;1996年02期
10 孙建伦,王刚,王福,左良,梁志德;IF钢在α→γ→α相变过程中取向对应关系[J];东北大学学报;1998年05期
相关会议论文 前4条
1 孙峰;李金山;寇宏超;唐斌;常辉;蔡建明;周廉;;Ti60钛合金α相溶解动力学及固溶组织特征[A];第十四届全国钛及钛合金学术交流会论文集（上册）[C];2010年
2 朱玉斌;王卫民;N.J.Park;H.J.Bunge;;CuZnAlTiSMA加工过程中α相织构的变化[A];首届中国功能材料及其应用学术会议论文集[C];1992年
3 雷力明;黄旭;孙福生;曹春晓;;热处理对Ti-25V-15Cr-2Al-0.2C-x阻燃β钛合金中α相析出行为的影响[A];2002年材料科学与工程新进展（下）——2002年中国材料研讨会论文集[C];2002年
4 杝文翰;灻i
本文编号：2436107
本文链接：https://www.wllwen.com/kejilunwen/jiagonggongyi/2436107.html