正火对汽车齿轮锻坯性能的影响

发布时间：2019-03-08 11:27

【摘要】：对齿轮锻坯进行了三种不同工艺的正火处理,并进行了耐磨损性能和力学性能的测试与分析。结果表明,与常规正火相比,等温正火试样的磨损体积减小35%,抗拉强度、屈服强度和断后伸长率分别提高13%、25%、27%;磁场正火试样的磨损体积减小63%,抗拉强度、屈服强度和断后伸长率分别提高28%、38%、46%。汽车齿轮锻坯正火工艺优选磁场正火工艺。
[Abstract]:The normalizing treatment of gear forging billet with three different processes was carried out, and the wear resistance and mechanical properties were tested and analyzed. The results showed that the wear volume of isothermal normalizing sample decreased by 35%, and the tensile strength, yield strength and elongation after break increased by 13%, 25% and 27%, respectively. The wear volume decreased by 63%, tensile strength, yield strength and elongation after break increased by 28%, 38% and 46%, respectively. Optimization of magnetic field normalizing process for automobile gear forging billet.
【作者单位】： 包头职业技术学院;
【基金】：内蒙古自治区高等学校科学研究项目(NJZC14386)
【分类号】：TG156.4

【相似文献】

相关期刊论文 前10条

1 金荣植;;汽车齿轮热处理车间环保、安全防火、防爆的设计与安装[J];汽车工艺与材料;2009年07期

2 韩丕伟;;汽车齿轮的硝盐淬火[J];现代零部件;2011年02期

3 郑书芳;高永强;;前清洗对汽车齿轮热处理畸变的影响[J];金属加工(热加工);2011年17期

4 雯;;汽车齿轮包装防锈方法的改进[J];材料保护;1965年03期

5 周德华;;20MnMoB钢制造重型汽车齿轮的试验与应用[J];机械;1986年02期

6 ;轻型汽车齿轮工艺探析[J];机械科学与技术;1989年06期

7 方和杰;新型高效多用途淬火油在汽车齿轮淬火中的应用[J];金属热处理;1996年06期

8 黄丽荣;汤宏智;;汽车齿轮硬化层深的设计[J];热处理技术与装备;2008年06期

9 孙朝国;关于汽车齿轮花键孔推孔整形的研究[J];铸锻热;1998年02期

10 曹颖;韩克甲;刘露;;重卡汽车齿轮开裂失效分析[J];热处理技术与装备;2014年03期

相关会议论文 前1条

1 刘志儒;阎牧夫;王勇;江建明;唐宁;王冶;王鸿春;贾玉山;吴德斌;金永植;陈云生;;汽车齿轮渗碳存在问题与对策采用稀土共渗技术[A];2005年（西安）齿轮材料与热处理工艺技术发展研讨会齿轮热处理论文集[C];2005年

相关硕士学位论文 前2条

1 涂小龙;重型汽车齿轮热处理变形控制[D];浙江大学;2005年

2 赵亮;汽车齿轮滚齿切削过程研究及其工艺参数选择[D];哈尔滨理工大学;2006年

，

本文编号：2436760