6061-T6铝合金板材热冲压成形极限图研究

发布时间：2019-03-23 20:45

【摘要】：自行设计并研制了一套获取板材热冲压成形极限图的试验系统,开展了6061-T6铝合金板材在不同应变路径及温度下的成形极限研究,获得了其在25~300℃的成形极限图。使用MSC.MARC软件对6061-T6铝合金板材的热冲压成形进行数值模拟,研究了失稳判断方法对不同温度下成形极限预测的影响。结果表明:6061-T6铝合金在室温下的极限应变值很低,塑性较差;变形温度升高到200℃时,极限应变值平均提高了99.5%;变形温度从200℃升高到300℃时,极限应变值进一步提高了23.5%,其塑性也显著提高。采用最大载荷判断法和应变路径判断法相结合的失稳状态判断准则能准确预测6061-T6铝合金的热成形极限,模拟结果和试验结果吻合较好。
[Abstract]:A set of test system for obtaining forming limit diagram of sheet metal hot stamping was designed and developed. The forming limit of 6061-T6 aluminum alloy sheet at different strain paths and temperatures was studied, and the forming limit diagram at 25 鈩，