碳钢表面电泳沉积制备石墨烯及其在海水中防腐蚀性能研究

发布时间：2019-05-22 03:24

【摘要】：通过在石墨烯纳米碎片C750片层间掺杂H+,采用电泳沉积法在碳钢基体表面电泳沉积制备C750石墨烯层,运用SEM、XRD、Raman光谱等技术对C750石墨烯层的物理性能进行表征,并采用电化学方法对C750石墨烯沉积层在模拟海水环境下的防腐蚀性能及机理进行研究。结果表明:利用电泳沉积的方法可以在Q235碳钢基体上得到致密的C750石墨烯层,并且随着电解液中H~+-C750浓度的增加,此防护层的耐蚀性先提高后降低。C750石墨烯层主要通过改变阴极极化行为来起到防腐的作用。
[Abstract]:C750 graphene layer was prepared by electrodeposition on the surface of carbon steel substrate by doping H between graphene nanoparticles C750 lamellae. The physical properties of C750 graphene layer were characterized by SEM,XRD,Raman spectroscopy. The corrosion resistance and mechanism of C750 graphene deposit in simulated seawater environment were studied by electrochemical method. The results show that a dense C750 graphene layer can be obtained on Q235 carbon steel matrix by electrodeposition, and with the increase of H750 concentration in electrolyte, The corrosion resistance of the protective layer is improved at first and then decreased. The C750 graphene layer mainly plays an anticorrosion role by changing the cathodic polarization behavior.
【作者单位】： 武汉科技大学省部共建耐火材料与冶金国家重点实验室;江苏华能电缆股份有限公司;
【基金】：国家自然科学基金(51201119)~~
【分类号】：TG174.4

【参考文献】

相关期刊论文 前3条

1 何青;马爱斌;江静华;宋丹;陈建清;杨东辉;邹中秋;李玉华;;石墨烯的制备及其在金属防腐中的应用进展[J];功能材料;2013年S2期

2 彭黎琼;谢金花;郭超;张东;;石墨烯的表征方法[J];功能材料;2013年21期

3 ;Electrochemical reduction of graphene oxide films:Preparation,characterization and their electrochemical properties[J];Chinese Science Bulletin;2012年23期

【共引文献】

相关期刊论文 前10条

1 蒋涛明;黄峰;胡骞;刘静;乔文玮;;碳钢表面电泳沉积制备石墨烯及其在海水中防腐蚀性能研究[J];腐蚀科学与防护技术;2017年02期

2 佘祖新;范梅梅;黄平;姚翔宇;;热带海洋大气环境下制动盘防护工艺耐腐蚀性能分析[J];装备环境工程;2017年01期

3 姬安;王希;徐长妍;石小梅;连海兰;施礼纳;王心怡;郭露;;石墨烯/炭黑导电油墨的制备与性能研究[J];林业工程学报;2017年01期

4 林浩;;浅谈钢桥防腐的研究概况[J];山西交通科技;2016年04期

5 王凯歌;王晓;孟腾飞;;我国石墨烯涂料的研发概况[J];上海涂料;2016年03期

6 龚水水;光善仪;柯福佑;徐洪耀;;红外光谱法氧化石墨烯羧基官能团含量的测定[J];中国测试;2016年04期

7 赵波;姜莉;袁铭辉;符显珠;孙蓉;汪正平;;电化学法制备石墨烯及其复合材料[J];电化学;2016年01期

8 李f，

本文编号：2482638