钛对55%Al-43.5%Zn-Si熔池中底渣相形成的影响

发布时间：2019-07-10 10:21

【摘要】：为研究Ti对55%Al-43.5%Zn-Si熔池中底渣相形成的影响,采用金相显微镜、扫描电镜(SEM)及能谱仪(EDS),对不同Ti含量(0.02wt%、0.05wt%、0.10wt%、0.20wt%)下熔池中产生的金属间化合物进行形貌、大小、分布及成分分析。结果表明:当Ti含量为0.02wt%时,镀液中析出少量底渣相,尺寸为50~70μm;随着Ti含量的增加,析出的底渣相尺寸变大,当Ti含量增加到0.20wt%时,镀液析出大量底渣相且聚集成大块状,尺寸为200~500μm。当熔池中Ti含量为0.02%和0.05wt%时,底渣中生成了Al7Fe2Si金属间化合物,当Ti含量达到0.20 wt%时,生成了Al20Fe5Si2金属间化合物,还生成了Ti Al3金属间化合物。
[Abstract]:In order to study the effect of Ti on the formation of a 55% Al-43.5% Zn-Si bath, the morphology, size, distribution and composition of the intermetallic compound produced in the bath at different Ti content (0.02 wt.%, 0.05 wt.%, 0.10 wt.%, 0.20 wt.%) were analyzed by means of a metallographic microscope, a scanning electron microscope (SEM) and an energy dispersive spectrometer (EDS). The results show that when the content of Ti is 0.02 wt%, a small amount of bottom slag phase is precipitated in the plating solution, and the size is 50-70. m When the content of Ti in the molten pool is 0.02% and 0.05% by weight, the Al7Fe2Si intermetallic compound is generated in the bottom slag, and when the Ti content reaches 0.20% by weight, the Al20Fe5Si2 intermetallic compound is generated, and the Ti Al3 intermetallic compound is also generated.
【作者单位】： 河北科技大学材料科学与工程学院;中国钢研科技集团有限公司先进金属材料涂镀国家工程实验室;上海梅山钢铁公司技术中心;
【基金】：河北科技大学校立基金项目(82/1182098)
【分类号】：TG142.1

【相似文献】

相关博士学位论文 前4条

1 张刚;基于焊工经验的人与熔池交互行为解析及熔池形态控制研究[D];兰州理工大学;2017年

2 彭进;铝合金激光液态填充焊的匙孔与熔池动态行为研究[D];哈尔滨工业大学;2016年

3 马国龙;双焦点光纤激光焊接特性及熔池行为研究[D];哈尔滨工业大学;2017年

4 刘成财;铝合金EBW熔池行为及焊缝成形规律的数值模拟研究[D];哈尔滨工业大学;2017年

相关硕士学位论文 前6条

1 黄怡晨;激光熔覆喷嘴粉末汇聚特性及其与熔池相互作用研究[D];哈尔滨工业大学;2017年

2 贾雪;Inconel 718合金选区激光熔化流场及微熔池传质的研究[D];哈尔滨工业大学;2017年

3 赵汉宇;激光立体成形过程中粉末与熔池气液界面微观作用机制[D];长安大学;2017年

4 冷昊凯;窄间隙双缆式GMAW熔池流体行为研究[D];江苏科技大学;2017年

5 王益荣;旋转电弧窄间隙焊缝成形和应力场的数值模拟[D];江苏科技大学;2017年

6 曹庆南;铝合金激光+GMAW复合热源焊接熔池动态行为数值分析[D];江苏科技大学;2017年

，

本文编号：2512542