TiAlN/Cu Nanocomposite Coatings Deposited by Filtered Cathod

发布时间：2021-01-23 07:17

　　TiAlN/Cu nanocomposite coatings with Cu concentration of 0–1.4 at.% were deposited on the highspeed steel（HSS） substrates by filtered cathodic arc ion plating technique.The chemical composition,microstructure,morphology,adhesion strength,mechanical and tribological properties of the TiAlN/Cu coatings were characterized and analyzed.The results reveal that the coating structure and properties depend on not only the Cu concentration,but also the deposition condition.The addition of Cu significantl... 

【文章来源】：Journal of Materials Science & Technology. 2017,33(01)

【文章页数】：6 页

【文章目录】：
1. Introduction
2. Experimental
3. Results and Discussion
    3.1. Chemical composition and XPS analysis
    3.2. Phase and crystal structure
    3.3. Mechanical properties and tribological property
    3.4. Morphology and microstructure
    3.5. Adhesion strength
    3.6. Discussion
4. Conclusion


【参考文献】：
期刊论文
[1]Ti（C,N）晶粒尺寸对金属陶瓷表面物理气相沉积的TiAlN涂层的微观组织和性能的影响（英文）[J]. 肖雅,熊计,郭智兴,刘俊波,周黎明,叶俊镠,赵武.  Journal of Central South University. 2020(03)
[2]N2流量比对复合磁控溅射Zr-B-N薄膜结构和性能的影响[J]. 王铁钢,郭玉垚,唐宽瑜,刘艳梅,林伟,姜肃猛.  表面技术. 2018(11)
[3]热作模具钢CrTiAlSiN多元复合涂层的工业制备及性能研究[J]. 董卫萍,柳琪,王进,马大衍.  模具制造. 2018(01)

博士论文
[1]微弧区间伏安特性对Ti及TiN镀层结构与性能的影响[D]. 杨超.西安理工大学 2017

硕士论文
[1]DLC/AlTiN复合涂层的制备及摩擦学性能研究[D]. 黄瑞华.燕山大学 2019
[2]热作模具Cr基复合纳米硬质涂层的工业制备及热稳定性研究[D]. 柳琪.青岛理工大学 2018
[3]车架纵梁冲裁工艺改进及数值模拟[D]. 曹耀远.青岛理工大学 2017



本文编号：2994804