严有为,刘生发,范晓明,傅正义,基于SHS技术制备铸造钢基TiC
本文关键词：基于SHS技术制备铸造钢基TiC-Fe梯度复合涂层及其界面结构，由笔耕文化传播整理发布。
首页 > 专家 > 内容
文献名称：基于SHS技术制备铸造钢基TiC-Fe梯度复合涂层及其界面结构
前言： 基于自蔓延高温。采用X射线衍射(XRD)确定了合成涂层的相组成,并分别用光学显微镜(OM),扫描电镜(SEM)和电子探针(EPMA)分析了涂层的显微组织及其与钢基体的界面结构。实验结果表明,合成的涂层除表面2mm的区域外,其它部分均具有较致密的结构。而且,涂层中原位合成的TiC颗粒的数量和尺寸均沿涂层的厚度方向逐渐递减,直至与钢基体实现梯度复合。初步认为,浇铸的钢液向Ti-C-Fe预制块中的渗透以及预制块中Fe粉的熔化对上述梯度复合涂层的形成起到了积极的作用。
A TiCFe preform was preplaced in a mould cavity and then was directly ignited to bring about the selfpropagating hightemperature synthesis (SHS) reaction by the temperature of pouring liquid carbon steel. As a result, a TiCFe cermet coating with a thickness of 10 mm was simultaneously synthesized on the steel substrate during its casting. The phase constituents of the synthesized coating were inspected by Xray diffraction (XRD), and the microstructure of the coating, especially its interfacial struct...
文献名称 基于SHS技术制备铸造钢基TiC-Fe梯度复合涂层及其界面结构
Article Name
英文(英语)翻译
FABRICATION AND INTERFACIAL STRUCTURE OF TiC-Fe CERMET GRADED COMPOSITE COATING ON CAST STEEL SUBSTRATE BASED ON SHS TECHNOLOGY;
作者 严有为; 刘生发; 范晓明; 傅正义;
Author YAN Youwei1;LIU Shengfa2;FAN Xiaoming2;FU Zhengyi3Technology;Wuhan 430074;China;2.School of Materials Science and Engineering;Wuhan University of Technology;Wuhan 430070;Wuhan University of Technology;China）;
作者单位
Author Agencies
华中科技大学模具技术国家重点实验室;
武汉理工大学材料科学与工程学院;
武汉理工大学材料复合新技术国家重点实验室 武汉;
文献出处
Article From
中国科学院上海冶金研究所; 材料物理与化学(专业) 博士论文 2000年度
关键词 SHS; 铸造; TiC-Fe金属陶瓷涂层; 钢基; 梯度复合; 界面;
Keywords SHS;casting;TiC-Fe cermet coating;steel substrate;graded composite;interface;
CuO对重力分离SHS陶瓷内衬复合管组织的影响
静态SHS陶瓷内衬复合喷嘴的抗热疲劳性能研究
SHS法制备高性能Y_2O_3掺杂AlN陶瓷粉体
一维双核锌配合物[Zn_2(SHSH)_2(2-Me-py)_2]的合成、晶体结构及理论研究
MnFe加入对SHS负压铸造钢基表面复合材料的影响
预涂覆工艺对SHS陶瓷内衬复合管界面的影响
SHS法制备硼化物陶瓷粉体的表征分析
自蔓延高温合成(SHS)TiC-Al_2O_3陶瓷基蜂窝催化载体
重力SHS制备陶瓷内衬复合管中稀释剂使用原则的探讨
基于自蔓延高温合成(SHS)的涂层技术
本文关键词：基于SHS技术制备铸造钢基TiC-Fe梯度复合涂层及其界面结构，，由笔耕文化传播整理发布。
本文编号：87931
本文链接：https://www.wllwen.com/kejilunwen/jiagonggongyi/87931.html