Electrochemical corrosion resistance of CeO 2 -Cr/Ti coating

发布时间：2021-10-20 05:15

　　The pack cementation was employed to improve the electrochemical corrosion resistance of 304 stainless steel via CeO2-Cr modified Ti coatings. Continuous coatings were formed on 304 stainless steel surface by this method. A series of electrochemical experiments were carried out to investigate the corrosion resistance of 304 stainless steel, Ti coating and CeO2-Cr/Ti coatings. The sample surface was investigated by scanning electron microscopy（SEM）. The phases of sample surface were detected by X... 

【文章来源】：Journal of Rare Earths. 2015,33(10)EISCICSCD

【文章页数】：7 页

【文章目录】：
1 Experimental
    1.1 Materials
    1.2 Preparation of Ce O2-Cr/Ti coatings
    1.3 Electrochemical corrosion resistance tests
2 Results and discussion
    2.1 Microstructural characterization
    2.2 Electrochemical corrosion resistance in 3.5%Na Cl solution
3 Conclusions


【参考文献】：
期刊论文
[1]304不锈钢表面Mo合金化改性层组织结构及耐磨性研究[J]. 刘成松,秦林,李翠玲,尹研,贾亚斌,郭丽丽.  表面技术. 2014(05)
[2]TiO2薄膜的制备及其对304不锈钢防腐性能的研究[J]. 吴震弘,汪洋,冯佩,毛丽婷.  浙江理工大学学报. 2014(03)
[3]Vapor phase codeposition of Cr and Si on Nb-base in situ composites by pack cementation process[J]. Bifei Yuan,Yang Li,Min Qiao,Chungen Zhou.  Progress in Natural Science:Materials International. 2013(02)
[4]渗铬P110钢在CO2饱和模拟油田采出液中的耐蚀性[J]. 林乃明,谢发勤,吴向清,田伟.  沈阳工业大学学报. 2012(01)
[5]Influence of process parameters on thickness and wear resistance of rare earth modified chromium coatings on P110 steel synthesized by pack cementation[J]. 林乃明,谢发勤,吴向清,田伟.  Journal of Rare Earths. 2011(04)
[6]Microstructures and wear resistance of chromium coatings on P110 steel fabricated by pack cementation[J]. 林乃明,谢发勤,周俊,钟涛,吴向清,田伟.  Journal of Central South University of Technology. 2010(06)
[7]油气田CO2腐蚀的防护技术研究[J]. 熊颖,陈大钧.  全面腐蚀控制. 2007(04)
[8]稀土元素对钢渗铬层组织与性能的影响[J]. 林祥丰,张瑞容.  金属热处理学报. 1995(03)



本文编号：3446312