超声离心法钠化提纯膨润土
发布时间：2018-06-02 14:15
本文选题：膨润土 + 超声离心 ； 参考：《非金属矿》2017年03期
【摘要】：以四川三台、广西田东、新疆夏子街3个产地的膨润土为原料进行钠化提纯实验,对比重力沉降与超声离心两种不同钠化提纯工艺效果;探索离心转速、离心时间、钠化剂用量对钠化提纯效果的影响,通过物化性能的测试,比较提纯前后阳离子交换容量(CEC)、膨胀容、胶质价、吸蓝量。采用X-射线荧光、X-射线衍射仪分析原矿及提纯样品的化学成分和物相组成。结果表明,超声离心可以提高提纯效果,并且提纯后物化性能有大幅提升。
[Abstract]:Using bentonite from three producing areas of Santai, Guangxi Tian Dong and Xiazijie, Xinjiang as raw material, sodium purification experiments were carried out to compare the effects of gravity sedimentation and ultrasonic centrifugation, to explore centrifugation speed and time. The effect of the amount of sodium agent on the purification effect of sodium was studied. The cationic exchange capacity (CEC), swelling capacity, colloidal value and blue absorption amount were compared before and after purification by physical and chemical tests. The chemical composition and phase composition of raw ore and purified samples were analyzed by X ray fluorescence X ray diffractometer. The results show that ultrasonic centrifugation can improve the purification effect, and the physical and chemical properties of the purification can be greatly improved.
【作者单位】： 固体废物资源化教育部重点实验室;西南科技大学矿物材料及应用研究所;
【基金】：国家自然科学基金(41372052)
【分类号】：TD97
【相似文献】
中国期刊全文数据库 前10条
1 罗太安,刘晓东;广丰膨润土钠化改型研究[J];非金属矿;2004年03期
2 蒋冲,曹佳宏,石云良;桃源膨润土钠化改型研究[J];矿冶工程;2004年06期
3 李彩霞;任瑞晨;董庆国;王秀兰;;某膨润土钠化改性性能试验研究[J];辽宁工程技术大学学报(自然科学版);2009年04期
4 徐光亮;;鄂州膨润土湿法提纯及钠化改型试验研究[J];中国非金属矿工业导刊;2010年06期
5 林涛;任建晓;殷学风;;膨润土的钠化工艺研究[J];陕西科技大学学报(自然科学版);2013年03期
6 胡茂焱 ,郑秀华;膨润土的钠化及最优加碱量的确定[J];非金属矿;1991年03期
7 李永伦;王力;;钙基蒙脱土的钠化改型[J];矿产保护与利用;2007年02期
8 冯辉霞;张国宏;李春雷;邵亮;赵阳;张婷;邱建辉;邱明;;平凉钙基膨润土干法钠化工艺研究[J];非金属矿;2007年04期
9 李翠珍;任广元;高建卫;;有机钠盐对膨润土的钠化研究[J];矿产保护与利用;2007年04期
10 钟春龙;涂逢樟;吴|，
本文编号：1969058
本文链接：https://www.wllwen.com/kejilunwen/kuangye/1969058.html