铜冶炼炉渣浮选尾矿的硫酸浸出及动力学研究

发布时间：2018-06-05 03:35

  本文选题：铜冶炼 + 炉渣浮选尾矿　； 参考：《金属矿山》2017年12期

【摘要】：尾矿的大量囤积已成为制约冶炼过程可持续发展的重要因素,从尾矿中回收有价金属元素可以降低企业资源的过度浪费,减少对周边环境的污染,同时提高资源的综合回收率。对某铜冶炼炉渣浮选尾矿采用硫酸浸出工艺进行试验,考察了初始pH、液固比、浸出时间和浸出温度对铜浸出率的影响。结果表明:在初始pH=3、浸出时间为12 h、液固比为4 m L/g、浸出温度为90℃条件下,铜的浸出率达到78.53%,H2SO4用量为23.57 kg/t,其余杂质元素浸出率较低。对铜浸出过程动力学模型研究表明,该硫酸浸出过程符号内扩散模型,反应的表观活化能为23.961k J/mol。
[Abstract]:The heavy hoarding of tailings has become an important factor restricting the sustainable development of smelting process. The recovery of valuable metal elements from tailings can reduce the excessive waste of the enterprise resources, reduce the pollution to the surrounding environment, and improve the comprehensive recovery rate of the resources. The effect of initial pH, liquid-solid ratio, leaching time and leaching temperature on copper leaching rate, the results show that the leaching rate of copper is 78.53%, H2SO4 dosage is 23.57 kg/t, and the leaching rate of other impurities is low. The kinetics model of copper leaching process is studied at initial pH=3, the leaching time is 12 h, the liquid to solid ratio is 4 m L/g and the leaching temperature is 90. It shows that the apparent activation energy of the reaction is 23.961k J/mol. in the sulfuric acid leaching process.
【作者单位】： 江西理工大学冶金与化学工程学院;
【基金】：国家自然科学基金项目(编号:51564021) 江西省自然科学基金项目(编号:20151BAB206028) 江西省重点研发计划项目(编号:20171BBG70041)
【分类号】：TD923;TD926.4

【相似文献】

相关期刊论文 前8条

1 陈焱;路南;;锗镓矿石的硫酸浸出[J];世界采矿快报;1992年11期

2 张文钲;;硝酸硫酸浸出钼精矿现状和进展[J];钼业经济技术;1989年03期

3 张泽强,沈上越;光催化氧化预处理对硫酸浸出硫化铜精矿的影响[J];有色金属(选矿部分);2004年05期

4 郑占千;;浅析铜渣焙烧温度与焙砂硫酸浸出的关系[J];新疆有色金属;2010年S1期

5 文健;王琳;;锰结核矿的硫酸浸出[J];世界采矿快报;1990年02期

6 卡里诺;汪焰台;刘尚勇;;加拿大格尔夫矿物公司拉比特湖铀厂铀的回收[J];铀矿选冶;1980年06期

7 郑永兴;文书明;郑海雷;邓久帅;刘建;;含铜难处理铁矿的硫酸浸出试验研究[J];矿产综合利用;2011年01期

8 李金生;李杰;雷丽;王亮娟;樊占国;;富硼渣制备硼酸及回收硫酸镁的新研究[J];矿产综合利用;2011年03期

相关硕士学位论文 前1条

1 李涛;改性钨尾矿地聚合物的制备及其性能研究[D];江西理工大学;2017年

，

本文编号：1980310