钠基蒙脱土的有机改性及表征

发布时间：2018-09-09 10:25

【摘要】：分别采用3种有机改性剂十二烷基三甲基溴化铵(DTAB)、十六烷基三甲基溴化铵(CTAB)、十八烷基三甲基溴化铵(OTAB)改性钠基蒙脱土(Na-MMT),讨论了改性剂种类、改性剂与蒙脱土的质量比、反应溶液的pH值对有机化蒙脱土的结构和表面性能的影响。使用X射线衍射仪(XRD)、傅立叶变换红外光谱仪(FTIR)、接触角测试仪对样品进行综合分析,分析结果表明:OTAB较DTAB、CTAB的插层效果更好,其层间距达到2.50nm,且当改性剂用量为100mmol/100g蒙脱土,pH=6时,其改性效果最佳。
[Abstract]:Sodium montmorillonite (Na-MMT) was modified with (CTAB), octadecyl trimethylammonium bromide (OTAB), three organic modifiers, dodecyl trimethylammonium bromide (DTAB),) and montmorillonite (MMT), respectively. The types of modifiers and the mass ratio of modifiers to montmorillonite were discussed. The effect of pH value of reaction solution on the structure and surface properties of organic montmorillonite. The X-ray diffractometer (XRD), Fourier transform infrared spectrometer (XRD),) and (FTIR), contact angle tester were used to analyze the samples. The results showed that the intercalation effect of DTAB,CTAB was better than that of DTAB,CTAB, the intercalation distance was 2.50 nm, and when the dosage of modifier was 100mmol/100g montmorillonite pH = 6, The modification effect is the best.
【作者单位】： 西南科技大学四川省非金属复合与功能材料重点实验室-省部共建国家重点实验室培育基地;西南科技大学材料科学与工程学院;
【基金】：表面物理与化学重点实验室开放基金(SPCXT201302) 西南科技大学研究生创新基金(15ycx012)
【分类号】：TD985

【相似文献】

相关期刊论文 前10条

1 李容;蒋晓丽;何晓英;李江;;改性钠基蒙脱土修饰电极上百草枯的电化学行为及测定[J];应用化学;2009年07期

2 殷兰兰;周淑娥;孙芬芳;;钠基蒙脱土在涂料中增稠防沉降效果的研究[J];精细与专用化学品;2011年05期

3 张林;陈介南;刘进;胡进波;于文吉;;钠基蒙脱土的有机改性及其表征[J];复合材料学报;2009年05期

4 刘华斌;肖汉宁;;阳离子表面活性剂对钠基蒙脱土的插层改性研究(英文)[J];无机材料学报;2012年07期

5 曹玉红,韦藤幼,吴旋,童张法;微波辐射干法制备钠基蒙脱土[J];化工矿物与加工;2004年06期

6 刘红宇;刘翠云;吕本莲;罗洁;宋文生;张玉清;;钠基蒙脱土交联增稠剂的合成及性能[J];应用化学;2008年09期

7 曹杨;孙友谊;;聚丙烯/蒙脱土纳米复合材料的制备与性能研究[J];塑料;2008年06期

8 桂成胜;刘小青;吴(由页);王古月;朱锦;;钠基蒙脱土增强豆胶的耐水性研究[J];林产工业;2012年06期

9 索大鹏,陈志刚,杨娟;季铵盐插层钠基蒙脱土的工艺研究[J];硅酸盐通报;2004年04期

10 王庆国;张晓红;乔金梁;;钠基蒙脱土在丁腈橡胶中的剥离分散及性能影响[J];科学通报;2008年12期

相关会议论文 前1条

1 曹玉红;韦藤幼;吴璇;童张法;;微波强化制备钠基蒙脱土[A];第二届全国传递过程学术研讨会论文集[C];2003年

相关硕士学位论文 前1条

1 徐叶净;咸水越流过程中粘性土膜效应的实验研究[D];河北联合大学;2014年

，

本文编号：2232115