不同倾角预制裂纹缺陷与运动裂纹的相互作用

发布时间：2018-02-15 03:01

  本文关键词： 固体力学 动态应力强度因子 预制裂纹缺陷 动态焦散线 冲击荷载 三点弯曲梁　出处：《爆炸与冲击》2017年01期 　论文类型：期刊论文

【摘要】：为了研究运动裂纹与不同倾角预制裂纹缺陷之间的作用机制,采用数字激光动态焦散线方法对含不同倾角预制裂纹缺陷的三点弯曲梁进行冲击实验。研究结果表明,在冲击载荷作用下,预制裂纹缺陷尖端均产生了次生裂纹;当运动主裂纹与预制裂纹缺陷贯通时,次生裂纹不会立即起裂,而是经过0~10μs的能量积蓄后,次生裂纹才起裂;运动主裂纹应力强度因子峰值与次裂纹起裂时的应力强度因子值均随预制裂纹倾角的增大而增大。
[Abstract]:In order to study the mechanism of action between moving crack and precast crack defect with different inclination angle, the digital laser dynamic caustic line method is used to carry out the impact test of three-point bending beam with different dip angle precast crack defect. Under impact load, secondary cracks occur at the tip of prefabricated cracks, and when the main moving cracks are connected with the precast crack defects, the secondary cracks do not start to crack immediately, but after energy accumulation of 0 ~ 10 渭 s, the secondary cracks start to crack. The peak value of the stress intensity factor of the main moving crack and the stress intensity factor of the secondary crack increase with the increase of the prefabricated crack inclination.
【作者单位】： 中国矿业大学(北京)力学与建筑工程学院;
【基金】：国家自然科学基金项目(51374210) 中央高校基本科研业务费专项基金项目(2009QL15)
【分类号】：O346.1

【相似文献】

相关期刊论文 前5条

1 朱万成;逄铭璋;唐春安;黄志平;李慎刚;;含预制裂纹岩石试样在动载荷作用下破裂模式的数值模拟[J];地下空间与工程学报;2005年06期

2 杨圣奇;蒋昱州;温森;;两条断续预制裂纹粗晶大理岩强度参数的研究[J];工程力学;2008年12期

3 张社荣;孙博;王超;严磊;;双轴压缩试验下岩石裂纹扩展的离散元分析[J];岩石力学与工程学报;2013年S2期

4 邱一平;戚靖骅;吴雪萍;陈雷;;大理岩Ⅱ型断裂规律试验及数值模拟分析[J];上海交通大学学报;2011年04期

5 ;[J];;年期

相关会议论文 前2条

1 霍喜伟;孙丽新;袁鹏举;张婕;李春传;;异型坯预制裂纹试验研究[A];2007中国钢铁年会论文集[C];2007年

2 沙宁;宋彦琦;王晓;邱桂林;刘江;;大理岩中的预制单裂纹扩展贯通实验研究[A];北京力学会第18届学术年会论文集[C];2012年

相关硕士学位论文 前2条

1 李鹏飞;基于声发射和图像处理技术对类岩石材料破裂过程的模型试验研究[D];重庆大学;2015年

2 彭晨;带预制裂纹混凝土疲劳损伤研究及寿命预测[D];武汉理工大学;2013年

，

本文编号：1512268