定向有机玻璃裂纹扩展性能试验研究

发布时间：2018-03-15 06:04

  本文选题：有机玻璃　切入点：疲劳裂纹扩展　出处：《机械强度》2016年04期 　论文类型：期刊论文

【摘要】：有机玻璃由于具有较好的强度和透光性而广泛应用于飞机风挡及座舱盖等结构中,其抵抗裂纹扩展性能对飞机安全性及使用寿命具有重要的影响。采用中心裂纹拉伸(CCT)试样对三种定向有机玻璃进行了疲劳裂纹扩展试验,采用七点递增多项式法对试验结果进行处理,求得不同试验条件下定向有机玻璃疲劳裂纹扩展速率与应力强度因子的关系式,对比分析了相同条件下三种定向有机玻璃的疲劳裂纹扩展性能,考核了应力比及残余应力对疲劳裂纹扩展速率的影响,为飞机座舱盖航空有机玻璃选材、使用及维护提供了试验依据。
[Abstract]:Organic glass is widely used in aircraft windshield and cabin cover because of its good intensity and light transmittance. Its resistance to crack growth has an important effect on the safety and service life of aircraft. The fatigue crack growth tests of three oriented plexiglass samples were carried out by using the central crack tensile test (CCT) sample. The experimental results are processed by using the seven-point incremental polynomial method, and the relationship between fatigue crack growth rate and stress intensity factor of oriented plexiglass under different test conditions is obtained. The fatigue crack propagation properties of three oriented plexiglass under the same conditions are compared and analyzed. The effects of stress ratio and residual stress on fatigue crack growth rate are examined. The test basis is provided for use and maintenance.
【作者单位】： 第一飞机设计研究院;
【分类号】：O346.1

【相似文献】

相关期刊论文 前4条

1 计欣华;尚伟;陈金龙;秦玉文;;定向有机玻璃疲劳断裂性能的频闪法研究[J];实验力学;2011年05期

2 尚伟;计欣华;张博;;定向有机玻璃拉伸度的等达因法研究[J];机械强度;2012年04期

3 吕锡慈,罗和璋;用会聚偏振光测定双轴热拉伸有机玻璃板的双折射值的研究[J];高分子通讯;1980年01期

4 ;[J];;年期

相关会议论文 前2条

1 陈小刚;魏兵;惠战荣;;定向有机玻璃裂纹扩展性能研究[A];中国力学学会学术大会'2009论文摘要集[C];2009年

2 欧迎春;冯海兵;蓝知惟;马眷荣;;改善聚氨酯胶片与定向有机玻璃界面粘结强度的研究[A];中国硅酸盐学会玻璃分会2009年全国玻璃科学技术年会论文集[C];2009年

相关博士学位论文 前1条

1 尚伟;定向拉伸工艺增韧有机玻璃若干力学问题的实验研究[D];天津大学;2011年

相关硕士学位论文 前1条

1 尚伟;定向有机玻璃力学性能的实验和数值模拟研究[D];天津大学;2008年

，

本文编号：1614728