活性TH灰在C60钢板剪力墙混凝土中的应用研究

发布时间：2018-06-03 00:41

  本文选题：混凝土 + 活性TH灰　； 参考：《施工技术》2014年24期

【摘要】：以武汉绿地中心钢板剪力墙C60混凝土为研究对象,采用活性TH灰这一新型矿物掺和料进行试验,解决了高强混凝土黏度大、收缩大、温升高的难题。通过净浆试验与混凝土配合比设计,确定了活性TH灰掺量在15%时,混凝土的黏度、工作性、强度均较理想;与硅灰配制的混凝土进行体积稳定性对比试验,表明活性TH灰混凝土的体积稳定性具有明显优势;以活性TH灰掺量15%的配合比进行工程应用,结果表明混凝土各项指标达到设计要求,墙体表面平整,施工效果良好。
[Abstract]:Taking the C60 concrete of steel plate shear wall in Wuhan green space center as the research object, the problem of high strength concrete viscosity, large shrinkage and rising temperature is solved by using active th ash, a new mineral admixture. The viscosity, workability and strength of concrete are all ideal when the content of active th ash is 15, and the volume stability of concrete prepared with silica fume is compared with that of concrete prepared by silica fume. The results show that the volume stability of active th ash concrete has obvious advantages, and the mix ratio of 15% active th ash is used in engineering application. The results show that each index of concrete meets the design requirements, the wall surface is flat, and the construction effect is good.
【作者单位】： 中建商品混凝土有限公司;
【基金】：高强高性能混凝土超高泵送混凝土配制技术与测试评价体系的综合研究(CSCEC-2013-05)
【分类号】：TU528.31

【参考文献】

相关期刊论文 前4条

1 张文江;曹万林;董宏英;张建伟;;带栓钉钢板与外包混凝土剪力墙共同工作性能研究[J];北京工业大学学报;2012年06期

2 夏勇,裴若娟;高层剪力墙结构温度应力初探[J];建筑结构;2000年02期

3 王军;顾瑞;朱亚杰;任海波;;活性TH粉C50自密实钢管混凝土配制技术与应用[J];混凝土与水泥制品;2014年02期

4 姚武;郑欣;;配合比参数对混凝土热膨胀系数的影响[J];同济大学学报(自然科学版);2007年01期

【共引文献】

相关期刊论文 前10条

1 胡俊,汪忠明,方高倪;基于带有偏差单元的IRN模型的大体积混凝土温度预测与控制[J];安徽建筑工业学院学报(自然科学版);2005年01期

2 ;美国人想把施工企业每周工作日缩减到四天[J];工程质量;2008年02期

3 黎海南;;钢筋混凝土屋面板温度应力的探讨[J];工程质量;2008年03期

4 冯德成;张鑫;许永吉;;水泥稳定碎石排水基层级配和胶浆设计[J];公路;2011年01期

5 张艳聪;田波;彭鹏;何哲;;水泥混凝土线膨胀系数试验研究[J];公路;2011年09期

6 程选生,蔺全录,王翠琳,李慧雯;钢筋混凝土矩形贮液池温差效应的初探[J];甘肃工业大学学报;2001年04期

7 金伟良,叶甲淳,严家q，

本文编号：1970801