镍铁氧体插层膨胀石墨水泥基材料的电磁屏蔽性能

发布时间：2018-08-07 12:17

【摘要】：研究了膨胀石墨及镍铁氧体(NiFe2O4)插层膨胀石墨对水泥浆体电磁屏蔽性能的影响。利用同轴法兰法测试了填充不同改性石墨水泥浆体的电磁屏蔽效能。结果表明,填充镍铁氧体插层膨胀石墨水泥浆体的电磁屏蔽效能可在整个测试频段获得大幅提高,特别是显著改善了低频段(30~1 000 MHz)的电磁屏蔽性能。掺加15%镍铁氧体插层膨胀石墨水泥浆体的电磁屏蔽效能SE值最高可达26 dB。
[Abstract]:The effects of expanded graphite and nickel ferrite (NiFe2O4) intercalated expanded graphite on the electromagnetic shielding properties of cement paste were studied. The electromagnetic shielding effectiveness of different modified graphite cement paste was tested by coaxial flange method. The results show that the electromagnetic shielding efficiency of the intercalated expanded graphite cement paste filled with nickel ferrite can be greatly improved in the whole test frequency range, especially in the low frequency band (30 ~ 1 000 MHz). The electromagnetic shielding efficiency (SE) of the expanded graphite cement paste mixed with 15% nickel ferrite is up to 26 dB.
【作者单位】： 南京工业大学材料科学与工程学院;南昌大学材料科学与工程学院;
【基金】：江西省科技支撑资助项目(20111BBG7002-3)
【分类号】：TQ172.1

【参考文献】

相关期刊论文 前4条

1 张晏清;孙庆荣;;磁性膨胀石墨的制备及性能[J];材料导报;2007年05期

2 司琼,董发勤;掺短碳纤维和石墨混凝土的低频电磁屏蔽性能[J];硅酸盐学报;2005年07期

3 黄少文;陈光华;邓敏;唐明述;;石墨 碳纤维水泥基复合材料的电磁屏蔽效能[J];硅酸盐学报;2010年04期

4 吴泽;张达威;黄荣华;韩志东;张显友;;可膨胀石墨的制备及影响因素[J];哈尔滨理工大学学报;2007年02期

【共引文献】

相关期刊论文 前10条

1 谭宏斌;聂翔;马小玲;;高频电磁屏蔽水泥基复合材料研究[J];兵器材料科学与工程;2007年06期

2 贾瑛;任强富;李志鹏;张秋禹;;膨胀石墨基纳米镍、铁、钴化学镀制备复合吸波材料[J];材料保护;2009年08期

3 罗利华;冯启明;王维清;黄阳;张博廉;;磁性累托石的制备及其对含有机染料废水的吸附性能[J];材料导报;2011年08期

4 谭宏斌;马小玲;;导电混凝土的导电性能与应用研究[J];房材与应用;2006年04期

5 王光华;董发勤;贺小春;;氧化铁-石墨/ABS复合材料制备及电磁屏蔽性能[J];功能材料;2008年02期

6 蒋文俊;方劲;李哲f，

本文编号：2170002