氯离子对316L不锈钢临界点蚀温度的影响

发布时间：2018-03-12 08:51

  本文选题：不锈钢　切入点：临界点蚀温度　出处：《腐蚀与防护》2017年06期 　论文类型：期刊论文

【摘要】：在外加恒电位下,通过测腐蚀电流密度-温度曲线的方法研究了Cl~-含量对316L不锈钢临界点蚀温度(CPT)的影响。结果表明:在临界点蚀温度以下,试样表面钝化膜比较稳定,超过该温度后,试样表面开始发生点蚀。Cl~-含量越高,316L不锈钢临界点蚀温度越低,且表面的点蚀坑越多。现场的腐蚀产物分析表明,腐蚀产物表面稀疏,主要元素为O、Fe、C、Cl。现场生产水Cl~-质量浓度高达21.431g/L,对316L不锈钢的腐蚀极其严重。
[Abstract]:The effect of Cl-content on the critical pitting temperature (CPT) of 316L stainless steel was studied by measuring the corrosion current density-temperature curve under constant potential. The results show that the passivation film on the surface of 316L stainless steel is stable under the critical pitting temperature. When the temperature exceeds this temperature, the surface of the sample begins to undergo pitting. The higher the content of Cl--is, the lower the critical pitting temperature of stainless steel is, and the more pitting pits are on the surface. The analysis of corrosion products in the field shows that the surface of corrosion products is sparse. The main element is OFE CnCl. The concentration of Cl-mass in water is 21.431 g / L and the corrosion of 316L stainless steel is very serious.
【作者单位】： 西南石油大学石油与天然气工程学院;
【分类号】：TE983;TG172.9

【相似文献】

相关期刊论文 前5条

1 雷冰;马元泰;李瑛;王福会;常泽亮;谢俊峰;宋文文;周理志;;模拟高温高压气井环境中HP2-13Cr的点蚀行为研究[J];腐蚀科学与防护技术;2013年02期

2 王献f ;含铬油套管钢的CO_2腐蚀点蚀特征研究[J];全面腐蚀控制;2002年06期

3 孙冬柏,李静,俞宏英,路民旭,严密林,赵国仙;Ca~(2+)和Mg~(2+)对CO_2环境中点蚀形貌的影响[J];钢铁研究学报;2001年03期

4 张国超;林冠发;张涓涛;;超级13Cr油套管钢的点蚀行为研究[J];焊管;2013年07期

5 ;[J];;年期

相关硕士学位论文 前2条

1 王军;原油储罐底板内腐蚀环境中的点蚀行为研究[D];中国石油大学(华东);2014年

2 曹治栓;油罐底板点蚀深度的数值模拟预测研究[D];中国石油大学（华东）;2013年

，

本文编号：1600856