催化聚合工艺对萘沥青结构和性能的影响

发布时间：2018-05-24 16:16

  本文选题：精萘 + 萘沥青　； 参考：《湖南大学学报(自然科学版)》2017年06期

【摘要】：以精萘为原料,HF/BF3为催化剂,研究了催化聚合温度、催化聚合时间对合成萘沥青结构和性能的影响.采用红外光谱(IR)、核磁共振(NMR)、元素分析(EA)和质谱(MS)等分析方法对萘沥青分子结构进行表征.研究表明,随催化聚合温度的提高,保温时间延长,萘沥青软化点、结焦值和TI组分含量提高,芳香氢含量降低,非芳香氢尤其是H_β含量增大;且随催化聚合温度提高,萘沥青分子中的脂肪侧链中的甲基含量降低、环烷结构含量提高.
[Abstract]:The effects of polymerization temperature and polymerization time on the structure and properties of naphthalene pitch were studied using naphthalene as raw material and HF- / BF3 as catalyst. The molecular structure of naphthalene pitch was characterized by IR, NMR, EA and MS. The results show that with the increase of catalytic polymerization temperature and holding time, the softening point, coking value and TI component content of naphthalene asphalt increase, the aromatic hydrogen content decreases, and the non-aromatic hydrogen content, especially H _ 尾, increases, and with the increase of catalytic polymerization temperature, the content of aromatic hydrogen decreases, and the content of non-aromatic hydrogen increases with the increase of catalytic polymerization temperature. The content of methyl in the fatty side chain of naphthalene pitch decreased and the content of naphthene structure increased.
【作者单位】： 湖南大学材料科学与工程学院;
【分类号】：TE626.86

【参考文献】

相关期刊论文 前3条

1 吕春祥,凌立成,吕维明,乔文明,刘朗;催化改性萘的反应特性及产物分析[J];新型炭材料;1999年03期

2 郑嘉明，，王成扬，阮湘泉，郭崇涛;催化缩聚法制备萘沥青和中间相沥青[J];天津大学学报;1995年02期

3 宋怀河;陈晓红;刘朗;张碧江;;重质稠环芳烃的固体核磁共振光谱研究[J];化学学报;2001年07期

【共引文献】

相关期刊论文 前10条

1 陈石林;郭建光;周娩红;谭嘉朕;;催化聚合工艺对萘沥青结构和性能的影响[J];湖南大学学报(自然科学版);2017年06期

2 王旺;王利;夏发军;王俊东;岳孝阳;刘春玲;董文生;;煤沥青与丙脱渣油性能结构分析[J];石油沥青;2016年06期

3 崔保银;张伟;崔海涛;李振荣;赵亮富;;煤焦油制中温沥青的族组分及结构表征[J];炭素技术;2016年05期

4 刘r

本文编号：1929738