安徽铜陵师姑墩遗址出土原始瓷的初步分析研究

发布时间：2018-03-26 12:29

  本文选题：铜陵　切入点：师姑墩遗址　出处：《文物保护与考古科学》2017年01期

【摘要】：通过对铜陵师姑墩遗址出土的29件原始瓷进行的检测分析表明,师姑墩原始瓷胎为高硅低铝型,部分器物胎体的Fe_2O_3和TiO_2含量较高;釉属高温钙釉,釉中Mn和P含量相对较高,其可能由草木灰引入,部分器物釉中含较高的Fe_2O_3,致使釉色较深。这一结果为皖南地区先秦时期原始瓷手工业发展研究提供了新的科学依据。
[Abstract]:Through the examination and analysis of 29 pieces of raw porcelain unearthed from Shigudun site of Tongling, it is shown that the original porcelain foetus of Shigudun is of high silicon and low aluminum type, and the contents of Fe_2O_3 and TiO_2 in some parts of the placenta are high, and the glaze belongs to high temperature calcium glaze, and the contents of mn and P in the glaze are relatively high. It may be introduced by plant ash, and some of the glaze contains higher Fe2O3, which results in a deeper glaze color. This result provides a new scientific basis for the development of the handicraft industry in the pre-Qin period in southern Anhui.