【摘要】:本文的主要研究内容分为以下三个部分:第一部分,以表面活性离子液体[C16MIm]Br(十六烷基三甲基咪唑溴盐)对HZSM-5A型沸石进行负载,得到改性沸石SMZ。以此改性分子筛为载体,DOP为增塑剂制备了PVC膜磷酸一氢根(HPO42-)选择性电极,最佳膜组成为w(增塑剂)w:(PVC):w(载体)=65:30:5,膜电极对HPO42-表现出良好的响应性。电极的响应范围为1.0×10-2~1.0×10-9 mol/L,响应斜率为-24.7 mV/decade,检测下限为4.09×10-10 mol/L。电极具有选择性好、检测限低的优点,在使用过程中也表现出了良好的可行性。所研制的电极可以成功的应用于湖水、池塘水和自来水中磷的检测。第二部分,以亚胺(C8H16-CH=NH,C10H20-CH=NH)为负载物来改性HZSM-5A型沸石,得到两种改性分子筛SMZ-C8和SMZ-C10。以改性分子筛为载体,DOP为增塑剂制备了Pb2+选择性电极,在w(增塑剂):w(PVC):w(载体)=65:30:5的配比下的膜电极的响应性能最好。膜电极对Pb2+的响应范围分别为:1.0×10-2~1.0×10-6和1.0×10-3~1.0×10-8mol/L,响应斜率分别为25.89和28.57mV/decade,检测下限分别为5.89×10-7和6.08×10-9 mol/L,电极对大部分的金属阳离子具有抗干扰能力,可在一定的pH范围内使用。所研制的两种电极可以成功地应用于湖水、池塘水和自来水中铅离子含量的测定及土壤、化妆水、白酒和茶叶中铅的含量的测定。第三部分,以苯扎氯铵(BKC)、度米芬(DB)为原料分别与四氟硼酸钠(NaBF4)、四苯硼钠(NaTPB)合成了两种缔合物[BK][BF4]和[DB][TPB],并以它们为载体,分别以DOP、DBP为增塑剂,研制了一种新的PVC膜[BK]、[DB]选择性电极,最佳膜组成为:w(增塑剂):w(PVC):w(载体)=66:33:1。所制备的两种膜电极对BKC、DB的响应范围分别为:1.0×10-2~1.0×10-6mol/L、1.0×10-3~1.0×10-6mol/L,响应斜率分别为:55.74 mV/decade、53.49 mV/decade,检测下限分别为:5.38×10-7 mol/L、4.39×10-7 mol/L。这两种膜电极选择性好,抗干扰能力强,且可在一定的pH范围内使用。所研制的电极可以成功的应用于纸巾、牛奶及眼药水中BKC的检测和度米芬含片中度米芬含量的测定。
[Abstract]:The main research contents of this paper are as follows: in the first part, the modified zeolite SMZZ was obtained by loading HZSM-5A zeolite with surfactant ionic liquid [C16MIm] Br( cetyltrimethyl imidazolium bromide salt). The modified molecular sieve was used as the carrier of DOP as plasticizer to prepare PVC membrane HPO _ 42-selective electrode. The optimum membrane composition was w (plasticizer w / PVC / w). The membrane electrode showed a good response to HPO _ 42-. The response range of the electrode is 1.0 脳 10-9 mol / L, the response slope is -24.7 MV / L, and the detection limit is 4.09 脳 10-10 mol / L. The electrode has the advantages of good selectivity and low detection limit. The electrode can be successfully applied to the determination of phosphorus in lake water, pond water and tap water. In the second part, two kinds of modified molecular sieves SMZ-C8 and SMZ-C10 were obtained by modifying HZSM-5A zeolites with imine C8H16-CHN NH (NH). The PB2 selective electrode was prepared with modified molecular sieve as the carrier and DOP as the plasticizer. The membrane electrode has the best response performance under the ratio of w (plasticizer w / w) PVC / w (carrier = 65: 30: 5). The response range of the membrane electrode to PB2 is 1.0 脳 10-2 (1.0 脳 10-6) and 1.0 脳 10-8 mol / L respectively, the response slope is 25.89 and 28.57 MV / L, the detection limits are 5.89 脳 10-7 and 6.08 脳 10-9 mol / L, respectively. The electrode has anti-interference ability to most metal cations and can be used in a certain pH range. The two kinds of electrodes can be successfully applied to the determination of lead ion content in lake water, pond water and tap water, as well as in soil, make-up water, liquor and tea. In the third part, two kinds of association complexes [BK] [BF4] and [DB] [TPB] were synthesized with sodium tetrafluoroborate (NaBF4) and sodium tetraphenylborate (NaBF4), respectively, using benzalkonium chloride (BKCX) and Dumifen (DBB) as raw materials. A new PVC membrane [BK], [DB] selective electrode was prepared using DOPN-DBP as plasticizer, respectively. The best membrane composition is: 1: 6: 33: 1. The response range of the two kinds of membrane electrodes to BKCnDB is 1.0 脳 10-6 mol / L = 1.0 脳 10-6 mol / L respectively, and the response slope is 55.74 MV / L / L, 53.49 MV / L / L, respectively, and the detection limit is: 5.38 脳 10 ~ (-7) mol / L ~ (4.39) 脳 10 ~ (-7) mol 路L ~ (-1), and the detection limit is: 5.38 脳 10 ~ (-7) mol / L ~ (-1) = 4.39 脳 10 ~ (-7) mol 路L ~ (-1), respectively. These two kinds of membrane electrodes have good selectivity, strong anti-interference ability and can be used in a certain pH range. The electrode can be successfully used for the determination of BKC in tissue, milk and eye drops and the determination of moderate mifen content in Dumifen buccal tablets.
【学位授予单位】:郑州大学
【学位级别】:硕士
【学位授予年份】:2017
【分类号】:O657.1

【相似文献】

相关期刊论文 前10条

1 焦晓娟;电极法测定水中氟化物的几点体会[J];中国环境监测;2002年05期

2 王树藩;;电极事故分析及防断方法[J];铁合金;1988年03期

3 王延龄,王琦,张仕定;关于加罩电极罩作用机理的讨论[J];光谱学与光谱分析;2003年06期

4 沈国励,韩梅,刘虹,俞汝勤;维生素B_6选择性电极的研究[J];高等学校化学学报;1985年10期

5 潘玲;电极法测定粮食中氟的若干问题探讨[J];江苏环境科技;1994年01期

6 杜宝中,鲁国民,薛力;以锑电极作参比电极测定废水中硫化物[J];分析试验室;2002年01期

7 王莉;于寿进;;水中氟化物电极法测定的改进[J];江苏预防医学;2007年03期

8 杨伯宇;李春塘;宦国禾;;赖氨酸细菌电极的研制和应用[J];离子选择电极通讯;1984年04期

9 徐芬,沈国励,俞汝勤,谢锦云,张梅芬;动物组织膜L-维生素C电极的研究[J];药学学报;1990年05期

10 孙长清;许宏鼎;高茜;王成顺;周慧;;双酶麦芽糖电极的研制与应用[J];化学传感器;1990年01期

相关会议论文 前9条

1 于海忠;;电极法测定氯离子浓度在大连地区的正常分布[A];中国输血协会第四届输血大会论文集[C];2006年

2 张会刚;朱庆山;;改进的缔合物模型优化模拟KCl-MgCl_2,KCl-FeCl_2熔盐体系[A];2004年全国冶金物理化学学术会议专辑[C];2004年

3 王双强;白向茹;刘瑞丽;颜振宁;;以(4-溴-3-甲氧基苯)肼为载体的铬离子选择性电极的研制与应用[A];河南省化学会2012年学术年会论文摘要集[C];2012年

4 郭小丽;郭敏;王新东;;适用于深海研究的硫离子选择性电极[A];第十三次全国电化学会议论文摘要集(下集)[C];2005年

5 屠月弦;;开发医用离子选择性电极为医学生物学服务[A];首届中国仪器仪表学会医疗仪器分会学术会议论文集[C];1993年

6 张楠;牛利;;一种安培式离子选择性电极作为水相中镉离子传感器[A];中国化学会第28届学术年会第10分会场摘要集[C];2012年

7 赵中一;姚宗江;方锐;赵丽华;;固相反射散射分光光度法测定碲[A];中国化学会第八届多元络合物会议论文[C];2002年

8 郭小丽;郭敏;王新东;;适用于深海探测的硫离子选择性电极的制备及性能研究[A];2006年全国冶金物理化学学术会议论文集[C];2006年

9 张淼;林建涵;张彦娥;;基于离子选择性电极的土壤硝态氮快速检测方法研究[A];2007年中国农业工程学会学术年会论文摘要集[C];2007年

相关博士学位论文 前10条

1 卢强;涂层钛电极的制备及其降解废水中硝基苯的研究[D];南京理工大学;2011年

2 毕强;电化学处理有机废水电极材料的制备与性能研究[D];西安建筑科技大学;2014年

3 刘sチ,

本文编号:2012315


资料下载
论文发表

本文链接:https://www.wllwen.com/shoufeilunwen/boshibiyelunwen/2012315.html


Copyright(c)文论论文网All Rights Reserved | 网站地图 |

版权申明:资料由用户15482***提供,本站仅收录摘要或目录,作者需要删除请E-mail邮箱bigeng88@qq.com