异氰脲酸三缩水甘油酯改性脱细胞猪真皮基质的研究

发布时间：2018-01-11 04:06

本文关键词：异氰脲酸三缩水甘油酯改性脱细胞猪真皮基质的研究　出处：《功能材料》2015年15期 　论文类型：期刊论文

【摘要】：采用异氰脲酸三缩水甘油酯(TGIC)对脱细胞猪真皮基质(p ADM)进行交联改性,考察了反应温度、p H值、用量和反应时间对基质材料收缩温度的影响,对交联前后基质材料的表面形貌、红外、热稳定性、耐酶降解性、力学性能、接触角等物理化学性能进行了表征,检测了基质材料的细胞毒性。结果表明,当反应温度为37℃,p H值为9.2左右,反应16~20 h,TGIC用量为10%时,基质材料的交联程度最大,收缩温度高达84℃;基质材料经TGIC交联能显著提高其形态稳定性、机械强度、热稳定性、耐酶降解性和亲水性,同时仍具有良好的细胞相容性,细胞毒性评级为Ⅰ级。
[Abstract]:The isocyanuric acid three glycidyl ester (TGIC) on porcine acellular dermal matrix (P ADM) by crosslinking modification, the effects of reaction temperature, P value of H, the influence of amount and reaction time on the shrinkage temperature of matrix material, the morphology, the matrix material surface before and after crosslinking infrared, thermal stability, resistance to enzyme the degradation of mechanical properties, contact angle and other physical and chemical properties were characterized by the detection of the cytotoxicity of matrix material. The results show that when the reaction temperature is 37 DEG C, P H value is about 9.2, 16~20 h, TGIC dosage is 10%, the maximum degree of cross linkage matrix materials, the shrinkage temperature of up to 84 C; matrix material crosslinked by TGIC can significantly improve the morphological stability, mechanical strength, thermal stability, resistance to enzymatic degradation and hydrophilic, while still has a good biocompatibility, cell toxicity rating to the first level.

【作者单位】：四川大学制革清洁技术国家工程实验室;四川大学生物医学工程技术研究中心;
【基金】：国家自然科学基金资助项目(51473001) 中央高校科研基地引导专项资助项目(SCU2014d005)
【分类号】：R318.08
【正文快照】： 1引言脱细胞真皮基质是具有维持和诱导细胞再生的3D结构的生物支架材料,它能够模仿原生细胞外基质(EMC)的生理和机械功能[1]。目前,脱细胞猪真皮基质(p ADM)主要是由胶原纤维束构成的紧实且具有良好生物相容性的支架材料,已经广泛应用于临床中的大面积及深度烧伤[2-6]。而主要

【参考文献】