含纳米银聚丙烯网片的制备及其表征和力学性质的检测

发布时间：2018-03-06 19:54

  本文选题：纳米银　切入点：聚丙烯　出处：《重庆医科大学》2012年硕士论文　论文类型：学位论文

【摘要】：本文探索了制备含纳米银聚丙烯网片的方法。利用熔融共混法将纳米银与聚丙烯按不同的质量比例共混造粒，加工得到相应的含纳米银聚丙烯网片。对所得样本的表面形貌和力学性能进行测试，考察不同添加量的纳米银对样本力学性能的影响，，并观察纳米银在复合物中的团聚情况。结果表明：通过相应工艺能够制备出含纳米银聚丙烯网片；纳米银能在不明显增加网片重量的同时提高其力学性质，且未对纤维的成纤及纺织性能造成明显影响；纳米银的团聚情况与添加量正相关，但总体较少。该实验为获得抗菌医用聚丙烯网片提供了新的思路。
[Abstract]:In this paper, the preparation method of polypropylene mesh containing nano-silver was studied. The nano-silver and polypropylene were blended and granulated in different mass ratio by melt blending method. The surface morphology and mechanical properties of the samples were tested, and the effects of different amounts of nano-silver on the mechanical properties of the samples were investigated. The agglomeration of nano-silver in the composite was observed. The results showed that the nano-silver polypropylene mesh could be prepared by the corresponding process, and the nano-silver could not increase the weight of the mesh and improve its mechanical properties. The agglomeration of nano-silver has a positive correlation with the addition amount, but it is less. This experiment provides a new idea for obtaining antibacterial medical polypropylene mesh.
【学位授予单位】：重庆医科大学
【学位级别】：硕士
【学位授予年份】：2012
【分类号】：R318.08

【参考文献】

相关期刊论文 前10条

1 刘亚;程博闻;韦媛辉;;纳米银PP抗菌纺粘布的开发[J];纺织学报;2006年02期

2 王鸿博;王锦嫣;王强;;纳米银抗菌非织造布研究[J];纺织学报;2006年07期

3 张文钲,王广文;纳米银抗菌材料研发现状[J];化工新型材料;2003年02期

4 徐雄立;周美华;;含纳米银的明胶/壳聚糖纳米纤维的制备及其抗菌性能研究[J];化工新型材料;2010年02期

5 唐晓峰;杨振国;孙治平;朱涛;瞿涤;;纳米银及纳米银无纺布的制备及其抗菌性能的表征[J];化工新型材料;2010年05期

6 李基业,邓群,李涛,姚胜,黎沾良;改良Stoppa技术修补巨大腹壁切口疝和缺损(31例报告)[J];临床外科杂志;2004年03期

7 李基业;;疝修补材料类型及有关并发症[J];临床外科杂志;2006年11期

8 季平,赵彦生,谢克昌;无机纳米材料改性聚丙烯研究进展[J];兰州工业高等专科学校学报;2003年04期

9 高俊刚,王东,刘悦有,于茂赏;mPE弹性体/PP共混物的流变行为与力学性能[J];塑料工业;2003年03期

10 丁超;贾德民;何慧;郭宝春;宁凯军;;界面改性剂对聚丙烯/蒙脱土纳米复合材料结构与性能的影响[J];塑料;2007年03期

本文编号：1576249