超声波分散制备类球状银包铜粉的性能研究

发布时间：2018-02-08 17:13

  本文关键词： 银包铜粉 类球状 超声波分散 抗氧化性　出处：《热加工工艺》2017年10期 　论文类型：期刊论文

【摘要】：以类球状铜粉为基体,在超声波和机械搅拌分散条件下,采用液相还原法在铜粉表面沉积镀银层制备银包铜粉。观察其表观色泽,测试其松装密度、粒度分布、比表面积、导电性和抗氧化性。采用SEM/EDS、XRD表征银包铜粉的形貌、成分和相组成。结果表明:采用此种方案制备出的银包铜粉的颜色为银白色,银含量45.7%、松装密度1.62 g/cm~3、粒径D_(50)为8.290μm、比表面积为0.749 m~2/g,导电性能良好,抗氧化性能较佳,所制备的银包铜粉具有良好的应用前景。
[Abstract]:Silver coated copper powder was prepared on the surface of copper powder by liquid phase reduction under the condition of ultrasonic and mechanical agitation dispersion. The apparent color of silver coated copper powder was observed, and its loose density, particle size distribution and specific surface area were measured. The morphology, composition and phase composition of silver coated copper powder were characterized by SEM / EDS- XRD. The results showed that the color of silver coated copper powder prepared by this method was silver white. The silver content is 45.7%, the density of loose packing is 1.62 g / cm ~ (-3), the diameter of DZ _ (50) is 8.290 渭 m, the specific surface area is 0.749 mm2 / g, the conductivity is good, the oxidation resistance is good, and the silver coated copper powder has good application prospect.
【作者单位】： 昆明理工大学材料科学与工程学院;
【基金】：国家科技型中小企业创新基金资助项目(14C26215303257) 昆明理工大学分析测试基金资助项目(20140061)
【分类号】：TB331;TB383.3

【相似文献】

相关期刊论文 前10条

1 娄萃;蔡晓兰;;银铜粉的研制及性能的研究[J];南方金属;2006年06期

2 王玉棉;于梦娇;王胜;侯新刚;赵燕春;;超细铜粉的制备方法、存在问题及应用[J];材料导报;2007年S1期

3 胡敏艺;徐锐;王崇国;周康根;;超细球形铜粉的制备[J];功能材料;2007年10期

4 蔡报珍;;超细铜粉的制备及应用[J];江西有色金属;2008年04期

5 黄凌云;朱国才;池汝安;霍慧彬;;我国超细铜粉研究及生产现状[J];化学通报;2008年05期

6 王文清;;歧化反应制备超细铜粉[J];武汉工业学院学报;2008年02期

7 刘维平;邱定蕃;于月光;;超声场辅助矿浆电解法制备超细铜粉[J];中国有色金属学报;2008年07期

8 刘维平;;制备细铜粉的新方法[J];粉末冶金技术;2008年05期

9 王尚军;方晓祖;余宗宝;;超细球形铜粉的制备工艺研究[J];中国粉体技术;2009年01期

10 薛丽梅;李双志;刘，

本文编号：1495949