多形态PPy膜界面聚合增长机理研究

发布时间：2018-06-17 20:48

  本文选题：聚吡咯 + 界面聚合　； 参考：《化工新型材料》2017年08期

【摘要】：在相转移催化剂(PTC)冠醚(CE)18C6的辅助下,采用界面聚合的方法,以三氯化铁(FeCl_3·6H_2O)作氧化剂,吡咯为单体,制备聚吡咯(PPy)薄膜。利用红外光谱测试、紫外-可见光测试和扫描电镜测试对聚合反应过程进行了跟踪,对聚合产物性能进行了表征。提出了基于成核-增长的吡咯界面聚合增长机理,并解释水相侧PPy典型的珊瑚形貌的形成过程;提出了缺陷尺寸控制的增长机理,并解释了油相侧具有不同形貌PPy的形成过程。
[Abstract]:The polypyrrole (Py) thin films were prepared by interfacial polymerization with the support of phase transfer catalyst PTC (PTC) crown ether CE-18C6, using FeCl _ 3H _ 2O _ 2O as oxidant and pyrrole as monomer. The polymerization process was tracked by IR, UV-Vis and SEM, and the properties of the polymerization products were characterized. The growth mechanism of pyrrole interfacial polymerization based on nucleation and growth was proposed, and the formation process of typical coral morphology in aqueous phase PPy was explained, and the growth mechanism of defect size control was put forward, and the formation process of PPy with different morphologies on oil side was explained.
【作者单位】： 西安科技大学材料科学与工程学院;
【基金】：国家自然科学基金项目(21204072) 陕西省重点科技创新团队项目(2014KCT-04)
【分类号】：O633.5;TB383.2

【相似文献】

相关期刊论文 前2条

1 刘新明;崔元臣;;界面聚合及其应用进展[J];化学研究;2006年01期

2 张浩勤,刘金盾,范国栋,方文骥;界面聚合制备复合膜过程的数学模型[J];高校化学工程学报;2004年02期

相关会议论文 前2条

1 周传强;宋根萍;郭荣;;表面活性剂排列为模板固/液界面聚合制备形貌可控的聚苯胺纳米结构[A];中国化学会第二十五届学术年会论文摘要集（下册）[C];2006年

2 纪红兵;李俊丽;裴丽霞;匡进高;;界面聚合制备纳米金属盐和金属用于固体催化剂[A];第十三届全国催化学术会议论文集[C];2006年

，

本文编号：2032403