气雾化制备微细球形钴铬钼钨合金粉末及其SLM成形性能

发布时间：2018-06-18 10:42

  本文选题：钴铬钼钨合金粉末 + 气雾化　； 参考：《粉末冶金材料科学与工程》2017年01期

【摘要】：利用自行研制的防返风超音速气雾化设备制备钴铬钼钨合金粉末,对粉末的形貌、粒度与粒度分布以及显微组织等进行分析,并研究其激光选区熔化成形件的显微组织、硬度和拉伸性能。结果表明,气雾化制备的Co Cr Mo W合金粉末主要为球形,部分有卫星颗粒,粉末组织由胞状晶和树枝晶组成。激光选区熔化成形的成形件表面熔道搭接良好,表面粗糙度为11.0μm,相对密度达到98.7%,组织为γ马氏体和ε马氏体;抗拉强度为1 283 MPa,屈服强度为852 MPa,伸长率为7.9%,显微硬度HV达到398.8;拉伸断口呈现准解理断裂特征。
[Abstract]:Cobalt chromium-molybdenum tungsten alloy powder was prepared by using the self-made anti-wind supersonic atomization equipment. The morphology, particle size and distribution and microstructure of the powder were analyzed, and the microstructure of the laser selective melting forming part was studied. Hardness and tensile properties. The results show that the Co Cr Mo W alloy powder prepared by gas atomization is mainly spherical, some of which are satellite particles, and the structure of the powder is composed of cellular crystal and dendrite. The surface melt channel of the formed parts formed by laser selective melting is good, the surface roughness is 11.0 渭 m, the relative density is 98.7, and the microstructure is 纬 martensite and 蔚 martensite. The tensile strength is 1 283 MPA, the yield strength is 852 MPA, the elongation is 7.9, the microhardness HV is 398.8, and the tensile fracture is quasi-cleavage fracture.
【作者单位】： 华南理工大学国家金属近净成形工程技术研究中心;江西悦安超细金属有限公司;广州市越珑金属粉末有限公司;
【基金】：广东省科技攻关项目(2014B010129003) 广东省自然科学基金团队项目(2015A030312003) 广州市科技攻关项目(201605101612300)
【分类号】：TF123.71

【相似文献】

相关期刊论文 前8条

1 朱琦;王林;杨秦莉;王娜;;钼钨合金的组织和性能研究[J];中国钼业;2013年05期

2 于波;;钼钨合金腐蚀层的辉光光谱逐层分析[J];光谱学与光谱分析;1983年01期

3 李玲玲;电阻率和加工性能好的钼钨合金材料[J];中国钨业;1997年03期

4 杨扬;钼及碳含量对铌钼钨合金高温机械性能的影响[J];稀有金属与硬质合金;2005年03期

5 钟培全;;液晶显示器用钼钨合金接线材料[J];中国钼业;1996年03期

6 马捷,毕安园,王从曾,周美玲;化学气相沉积制备钼钨合金[J];真空科学与技术学报;2005年03期

7 ;综合信息[J];世界有色金属;2005年05期

8 ;[J];;年期

相关硕士学位论文 前1条

1 杨静;钼钨合金在液锌中腐蚀的分子动力学模拟[D];河北工业大学;2015年

，

本文编号：2035204