高压下多孔阳极氧化铝薄膜的制备与光学性能研究

发布时间：2018-06-25 15:19

  本文选题：多孔阳极氧化铝 + 高压　； 参考：《功能材料》2017年06期

【摘要】：利用电化学方法在丙二酸的乙二醇溶液中制备多孔阳极氧化铝,并通过控制溶液浓度对氧化铝的厚度、孔径、孔间距进行了调控。实验发现,在氧化电压为500V时制备出的氧化铝模板孔间距大,且色彩饱和度高,其UV-Vis反射波峰随着溶液浓度的增大产生红移。在浓度为1.5mol/L丙二酸的乙二醇溶液中,制备出的阳极氧化铝薄膜孔间距能够达到400nm,并且在红光区(约622nm处)其UV-Vis反射光谱存在一个极大峰值。
[Abstract]:Porous anodic alumina was prepared by electrochemical method in ethylene glycol solution of malonic acid. The thickness, pore size and pore spacing of alumina were controlled by controlling the concentration of the solution. It was found that the pore spacing and color saturation of the alumina template prepared at 500 V were large, and the UV-Vis reflection peak shifted red with the increase of solution concentration. In ethylene glycol solution with 1.5 mol / L malonic acid concentration, the pore spacing of the anodic alumina film can reach 400 nm, and there is a maximum peak value of UV-Vis reflectance in the red region (about 622nm).
【作者单位】： 河北工业大学理学院应用物理系;
【基金】：国家自然科学基金资助项目(11547250) 河北省自然科学基金资助项目(A2015202343) 河北省科技厅研究项目(15211043)
【分类号】：TB383.2;TQ133.1

【相似文献】

相关期刊论文 前10条

1 常晓仆;李淑英;;多孔阳极氧化铝膜在分离方面的研究进展[J];四川化工;2006年02期

2 梁钜松;刘亚;叶能;徐勇勇;;多孔阳极氧化铝形成机理新解释[J];科技视界;2014年16期

3 姚素薇;孔亚西;张璐;;高度有序多孔阳极氧化铝膜形成机理的探讨[J];功能材料;2006年01期

4 王伟;梁淑敏;周淑清;;多孔阳极氧化铝膜的制备工艺研究[J];应用科技;2006年04期

5 张霞;胡明;孟宪权;;制备工艺对多孔阳极氧化铝特性的影响[J];武汉大学学报(理学版);2009年05期

6 黄伯贤;井红旗;;多孔阳极氧化铝膜的生长规律[J];河北师范大学学报;2006年03期

7 马迪;李淑英;;影响多孔阳极氧化铝膜结构特性因素的研究[J];电镀与精饰;2006年01期

8 杨培霞,安茂忠,郑铁帅;硫酸/草酸混酸电解液中阳极氧化法制备多孔阳极氧化铝模板[J];无机化学学报;2005年12期

9 马凯迪;谢宁;王倩;;不同退火条件对多孔阳极氧化铝热释光的影响[J];新疆大学学报(自然科学版);2014年01期

10 徐国荣;任凤莲;司士辉;;无阻挡层多孔阳极氧化铝膜板的制备[J];功能材料;2006年04期

相关会议论文 前1条

1 屈叶青;张平;曾鸿燕;;多孔阳极氧化铝膜制备新工艺[A];第三届全国化学工程与生物化工年会论文摘要集（下）[C];2006年

相关硕士学位论文 前1条

1 王昱扬;利用超薄有序多孔阳极氧化铝模板制备贵金属纳米材料及其在表面增强拉曼散射中的应用[D];吉林大学;2015年

，

本文编号：2066472